Abstract:Ultralong Cu@carbonaceous submicrocables with diameters of 0.4-0.6 mu m and lengths up to and exceeding 100 mu m have been fabricated successfully by a poly(vinyl alcohol)- (PVA-) assisted hydrothermal carbonization process using copper chloride and maltose as materials. In this one-pot synthesis, poly(vinyl alcohol) (PVA) played an important role in the formation of these submicrocables as a structure-directing agent to effectively restrain the formation of carbonaceous spheres that are normally nucleated from bulk solutions. In addition, the combined synergistic effects of both the carbohydrates and the PVA enable the formation of elegant Cu@carbonaceous submicrocables. Furthermore, control of the initial pH value (similar to 7-8) and reaction temperature (similar to 180 degrees C) is also essential for the formation of cablelike structures. The effects of other saccharides such as glucose, beta-cyclodextrin, and starch on the formation of Cu@carbonaceous submicrocables were also examined under similar conditions. The thermal stability of as-prepared Cu@carbonaceous submicrocables was studied. In addition, removal of the copper cores of Cu@carbonaceous submicrocables at ambient temperature in a mixed solution of hydrochloric acid and H2O2 can form well-defined amorphous carbonaceous submicrotubes.

Synthesis, Characterization, and Formation Mechanism of Copper Sulfide-Core/Carbon-Sheath Cables by A Simple Hydrothermal Route

Synthesis of Copper-Core/Carbon-Sheath Nanocables by a Surfactant-Assisted Hydrothermal Reduction/Carbonization Process

Synthesis and Characterization of CdS Based Sulfide Coaxial Cable and Nanotubes by Sacrificial Approach

Novel CuS Hollow Spheres Fabricated by a Novel Hydrothermal Method

Pva-Assisted Hydrothermal Synthesis Of Copper@Carbonaceous Submicrocables: Thermal Stability, And Their Conversion Into Amorphous Carbonaceous Submicrotubes

Copper sulfide micro-tubes fabricated by thermal evaporation of zinc sulfide

Fabrication and Characterization of Ag@C Nanocables with High Aspect Ratios by Hydrothermal Process

Facile synthesis of copper sulfide wire/carbon nanotube composite with improved sodium storage performance

Innovative Multiphase Ultrasonic-Assisted Method for High-Purity, Stable, and Cost-Effective Copper Nanowire Synthesis

Fabrication of copper sulfide microstructures with the bottle- and thorny rod-shape

Synthesis and characterization of multiwalled carbon nanotube/CdS core/shell heterostructures

Facile Sulfurization under Ambient Condition with Na2S to Fabricate Nanostructured Copper Sulfide

One-Step Synthesis Of Single-Wall Carbon Nanotube-Zns Core-Shell Nanocables

Cuo Nanodendrites Synthesized by A Novel Hydrothermal Route

Phase-Selective Synthesis and Self-Assembly of Monodisperse Copper Sulfide Nanocrystals

Electrochemical Synthesis of Copper Sulfide Nanostructure with PAM Hydrogel Template

Hydrothermal Synthesis of Cobalt Sulfide Nanotubes: the Size Control and Its Application in Supercapacitors

Low-temperature chemical solution route for ZnO based sulfide coaxial nanocables: general synthesis and gas sensor application

Surfactant-free hydrothermal synthesis of Ag/C nanocables

Synthesis of copper/cross-linked poly(vinyl alcohol)(PVA) nanocables via a simple hydrothermal route

Formation Of Transition-Metal Sulfide Microspheres Or Microtubes