Abstract:Uniform ZnO nanobelts and toothed-nanobelts were synthesized respectively through pure zinc powder evaporation without catalyst at temperature of 600 degrees C. In each processing, the total gas flow rate of argon and oxygen was 200 similar to 300 cm(3) (.) min(-1), and the fraction of oxygen was 1% similar to 5% according to changes of the conditions. The experiments indicated that the key of the preparation method is to control the flow rates and partial pressures of argon, oxygen, and zinc vapor. The flow rates and partial pressures influenced the size of nanostructures, and more sensitively determined the belts with or without teeth.Scanning electron microscopy(SEM) observations showed that the fabricated ZnO nanobelts had several types in morphology. The high-resolution transmission electron microscopy (HRTEM) images and selected area electron diffraction (SAED) patterns revealed that the ZnO nanobelts were single crystalline. HRTEM images and SAED patterns also suggested that the teeth of the toothed-nanobelts grew along the [0001] or [21 10] direction, i. e., the teeth of such belts may grow in "c" or "a" direction, the backbones of the belts may grow in "a" or "c" direction accordingly. X-ray diffraction (XRD) investigations on the structures showed that all the deposited nanobelts on the silicon substrate were pure ZnO with hexagonal wurtzite structure. Investigations through HRTEM and XRD indicated that the growth of ZnO nanobelts was controlled by vapor-solid(VS) mechanism.Photoluminescence(PL) spectrum of ZnO toothed-nanobelts at room temperature was measured and showed a UV emission at similar to 390 nm and a broad green emission with 4 subordinate peaks at 455 similar to 495 nm.

Porous ZnO Nanobelts: Synthesis, Mechanism, and Morphological Evolutions

Facile Fabrication of Porous ZnO by a Template Free Method

Porous ZnO nanobelts evolved from layered basic zinc acetate nanobelts

From Layered Basic Zinc Acetate Nanobelts to Hierarchical Zinc Oxide Nanostructures and Porous Zinc Oxide Nanobelts

Facile Solution Synthesis and Characterization of Zno Mesocrystals and Ultralong Nanowires from Layered Basic Zinc Salt Precursor

Porous and Single-Crystalline ZnO Nanobelts: Fabrication with Annealing Precursor Nanobelts, and Gas-Sensing and Optoelectronic Performance

Polymorphous ZnO nanostructures: Zn polar surface‐guided size and shape evolution mechanism and enhanced photocatalytic activity

Fabrication, Structures and Optical Property of Zno Nanobelts Prepared by A Novel Zn-Powder Evaporation Technique

Structural and Optical Properties of Porous ZnO Nanorods Synthesized by a Simple Two-Step Method

Complex and oriented ZnO nanostructures

Morphology-controllable electrochemical synthesis and photoluminescence properties of ZnO nanocrystals with porous structures

Morphology Evolution of One-Dimensional-Based ZnO Nanostructures Synthesized via Electrochemical Corrosion

Fabrication of ZnO with tunable morphology through a facile treatment of Zn-based coordination polymers

Porous ZnO Sheets Transformed from Zinc Sulfate Hydroxide Hydrate and Their Photoluminescence Performance

Assembly-line flash synthesis of ZnO nanobelts on metal Zn

Novel Single-Crystalline Hierarchical Structured Zno Nanorods Fabricated Via A Wet-Chemical Route: Combined High Gas Sensing Performance with Enhanced Optical Properties

Nanoplate-assembled hierarchical cake-like ZnO microstructures: solvothermal synthesis, characterization and photocatalytic properties

Large Scale Synthesis of Porous ZnO Hollow Structures with Tunable Diameters and Shell Thicknesses

A Simple Route to Porous ZnO and ZnCdO Nanowires

Preparation and Optical Properties of ZnO Comb-like Nanobelts

Morphology Evolution of One-Dimensional ZnO Nanostructures Towards Enhanced Photocatalysis Performance