Properties of the Calcium Phosphate Cement/PHBV Microspheres Composites

Liu Hailan,Limin Dong,Wang Chen,Qingfeng Zan,Jiemo Tian,HL Liu,LM Dong,C Wang,QF Zan,JM Tian

DOI: https://doi.org/10.3321/j.issn:1002-185x.2007.z2.012

2007-01-01

Rare Metal Materials and Engineering

Abstract:A new calcium phosphate cement composites were developed by adding PHBV microspheres, which had higher compressive strength in the early days and had three-dimensional pore structure in the later days due to degradation of PHBV microspheres. In the cement, the solid component was alpha-TCP, the liquid component was NaH2PO4/Na2HPO4 solution or KH2PO4/K2HPO4 solution, and the diameter of PHBV microspheres is about 100 mu m similar to 300 mu m. The effect of the liquid component, the ratio of the solid component and the liquid component and the proportion of PHBV microspheres on the setting time and the compressive strength were studied. The final setting times were 15 minutes similar to 30 minutes, and the compressive strengths were 10 MPa similar to 30 MPa. The properties of the composites indicated that the materials could be used as bone repair materials.