Abstract:Causes of a last stage blade's fracture of a certain power plant's 135 MW single reheat condensing steam turbine is being analyzed.By analyzing,scrutinizing and studying the main op-erational parameter data,the blade's strength,the material's composition,macroscopic apperance and metallographic structure of the blade's fracture surface,etc.after the occurence of the fracture,as well as the state existing before fracture,it was concluded that a foreign metallic body sticking on the blade's leading edge at about the height of 508 mm had caused stress concentration,and thus became the origin of fatigue cracks which eventually led to the blade's fracture.Figs 12,tables 3 and refs 7.

Fracture Analysis of a 135MW Steam Turbine's Last Stage Blade