Abstract:High frequency manganese-zinc ferrite was prepared by oxide ceramic process. The microstructure of representative samples was analyzed by scanning electron microscope (SEM). In addition, the resistivity (p) of samples was tested by YY2812 LCR meter and the magnetic properties were obtained by SY-8232 B-H Analyzer. In combination with the microstructure analysis of material, the effects of SnO 2 additive in MnZn ferrite were investigated, especially on initial permeability (μ i ), resistivity (p), hysteresis loss (P h ), eddy current loss (P e ) and residual loss (P r ). The results show that the amount of SnO 2 additive has an obvious influence on the microstructure and electromagnetic properties of the proposed material, such as μ ι , p, P h , P c and P r . There is an optimum content of SnO 2 which is 0.1% to ensure finer microstructure and lower loss at the frequency of 1MHz.

Effect of Tin Additive on the Microstructure and Loss of Ferrite for Switching Mode Power Supply