Stability and optimum polymerized condition of polysiloxane-polyacrylate core/shell polymer
ChengYue Ge,Yumin Wu,Jun Xu
DOI: https://doi.org/10.1002/adv.20182
IF: 2.5022
2010-01-01
Advances in Polymer Technology
Abstract:The stable emulsion of core/shell latex with little coagulum (no more than 0.5% in quality relative to total monomers) has been prepared at low temperature with potassium-persulfate (KPS), sodium formaldehyde sulfoxylate (SFS), and 2,2 '-azobis(2-(2-imidazolin-2-yl) propane) dihydrochloride (VA-044) as composite initiators by staged emulsion polymerization. Reactive surfactants were used to significantly improve the stability of emulsion. More interestingly, reverse core/shell structure was investigated when the organic silicon was added in the late period of polymerization. The effects of the emulsifier, initiators, dosage of organic silicon, and monomer's content on conversion and graft efficiency were studied in detail. Moreover, the stability of emulsion was investigated by the values of zeta potential (zeta) and coagulum. More importantly, the thermal performance and stability of PSI/PA composite latex was studied by the glass transition temperature (T(g)). The results showed that there are appropriate values for all factors to obtain high conversion, graft efficiency, and excellent stability: The dosage of surfactant was about 0.44 g, the dosage of VA-044 was about 1000 mg kg(-1), the dosage of organic silicon was about 15%, and the monomer's content was about 30%. In addition, the introduction of organic silicon improved the T(g). (C) 2010 Wiley Periodicals, Inc. Adv Polym Techn 29: 161-172, 2010; View this article online at wileyonlinelibrary.com. DOI 10.1002/adv.20182