Electrochemical and hot corrosion behaviour of steel reinforced with AlSiBeTiV high entropy alloy using friction stir processing

Ragunath Sundaram,Radhika Nachimuthu,Aravind Krishna Sivanandam,Jeyaprakash Natarajan
DOI: https://doi.org/10.1080/14686996.2024.2320083
IF: 7.821
2024-02-29
Science and Technology of Advanced Materials
Abstract:A lightweight AlSiBeTiV high entropy alloy (HEA) powder is synthesized by the ball milling process and is reinforced on SS410 through friction stir processing (FSP). Subsequently, the annealing process is conducted on the processed samples at 450, 600, and 750°C for 120 mins. The grains are refined at 600°C by 23.3% than the processed HEA sample. A higher microhardness of 672 HV is attained on the processed HEA sample annealed at 600°C due to the synergistic effect of FSP and annealing through refined grains. The electrochemical corrosion under a 3.5 wt.% NaCl environment, and the hot corrosion under the salt mixture environments of 75% Na 2 SO 4 +25% NaCl, and 60% Na 2 SO 4 +20% NaCl + 20% V 2 O 5 at 800°C for 50 h are investigated on the processed samples. The microstructure, induced corrosion products, and elemental distribution of the corroded surface of the annealed processed HEA sample are evaluated by morphological analysis. The induced oxidation effect enhances the Cr 2 O 3 and TiO 2 films on the corroded surfaces leading to higher corrosion resistance. A high corrosion resistance appears on the annealed processed HEA sample through the formation of a stable passive layer, hindering the pitting corrosion mechanism, grain refinement, and homogeneous distribution. So far, the majority of work focuses on Al and composites. However, the current work made a surface modification on SS410 steel by reinforcing lightweight HEA particles through friction stir processing followed by the annealing process.
materials science, multidisciplinary
What problem does this paper attempt to address?
The paper aims to address the following issues: 1. **Surface Modification and Material Strengthening**: Introducing lightweight high-entropy alloy (AlSiBeTiV HEA) on the surface of SS410 stainless steel through Friction Stir Processing (FSP) and improving its microstructure through subsequent annealing treatment. 2. **Corrosion Behavior Study**: Investigating the electrochemical corrosion and high-temperature corrosion behavior of HEA-reinforced steel treated with FSP and annealing under different temperature and salt environment conditions. Specifically, the focus of the paper is on: - Preparing lightweight AlSiBeTiV high-entropy alloy powder using ball milling and reinforcing it onto the SS410 stainless steel substrate through Friction Stir Processing. - Annealing the processed samples, maintaining them at 450°C, 600°C, and 750°C for 120 minutes. - Studying the effect of annealing treatment on the microhardness and corrosion performance of the material. - Conducting electrochemical corrosion tests in 3.5 wt.% NaCl solution and high-temperature corrosion tests using two different salt mixtures at 800°C. - Evaluating the performance of the annealed samples through microstructure analysis, element distribution, and corrosion product assessment. The main contributions of the paper are: - The first attempt to use Friction Stir Processing technology to reinforce lightweight high-entropy alloy particles onto the surface of SS410 stainless steel and further optimize its performance through annealing treatment. - Exploring the impact of different annealing temperatures on the material's microstructure and corrosion behavior.