Enhancing the Cycling Stability by Tuning the Chemical Bonding between Phosphorus and Carbon Nanotubes for Potassium-Ion Battery Anodes
Daqing Peng,Yaxin Chen,Heli Ma,Lei Zhang,Yi Hu,Xueni Chen,Yongli Cui,Yueli Shi,Quanchao Zhuang,Zhicheng Ju
DOI: https://doi.org/10.1021/acsami.0c11577
2020-07-27
Abstract:Phosphorus/carbon (P/C) composites as promising potassium-ion storage materials have been extensively investigated for its compound superiorities of high specific capacity and favorable electronic conductivity. However, the effects of different chemical bonding states between P and the carbon matrix for potassium-ion storage and cycling performance still need to be investigated. Herein, three P/C composites with different chemical bonding states were successfully fabricated through simply ball-milling red P with carboxylic group carbon nanotubes (CGCNTs), carbon nanotubes (CNTs), and reduced carboxylic group carbon nanotubes (RCGCNTs), respectively. When used as potassium-ion battery (PIB) anodes, the red P and CGCNT (P-CGCNT) composite deliver the most outstanding cycling stability (402.6 mAh g<sup>–1</sup> over 110 cycles) with a favorable capacity retention of 68.26% at a current density of 0.1 A g<sup>–1</sup>, much higher than that of the phosphorus-CNT (P-CNT) composite (297.5 mAh g<sup>–1</sup> and 50.40%). Based on the results of X-ray photoelectron spectroscopy and electrochemical performance, we propose that the existence of a carboxyl functional group will be instrumental for the formation of the P–O–C bond. More importantly, when compared with the P–C bond, the P–O–C bond can lead to a higher reversible capacity and a better long-term cycling stability as a result of the more robust bonding energy of the P–O–C bond (585 KJ mol<sup>–1</sup>) than that of the P–C bond (264 kJ mol<sup>–1</sup>). This work provides some insights into designing high-performance P anodes for PIBs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c11577?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c11577</a>.Experimental section (materials preparation, characterization, electrode fabrication, and electrochemical measurements) and details of GITT calculation, additional characterizations (SEM images of the P/C mixture, pristine P-CCGCNT and P-CNT composites, SEM and TEM images of the postcycling electrode, and XRD patterns), and additional electrochemical performances (CV profiles and d<i>Q</i>/d<i>V</i> curves) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c11577/suppl_file/am0c11577_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology