Abstract:In this work, we successfully report the design and synthesis of rod-like CoAl2O4/halloysite hybrid pigment from zeolitic imidazolate framework-67 (ZIF-67, a Co-based MOF) and tubular halloysite via a facile two-step route for the first time. The as-prepared nanostructures were thoroughly characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared reflection (FTIR Spectroscopy), thermogravimetric and differential scanning calorimetry (TG-DSC), X-ray photoelectron spectrometer (XPS), ultraviolet–visible spectrometry (UV–vis) and CIE L* a* b* colorimetric method. XRD patterns indicated that the presence of CoAl2O4 spinel was observed at various temperatures ranging from 800 to 1100 °C. The SEM and TEM images showed that the nano-pigment has a rod-like hybrid structure composed of nano CoAl2O4 particles and SiO2. The color performance of the fabricated pigments was evaluated and given suitable color coordinates (L* = 44.72, a* = −14.40, b* = −37.83) and (L* = 42.57, a* = −7.68, b* = −41.14) at the calcination temperature of 1100 °C for 2 h and 3 h, respectively. The mechanism study indicated that these composites were formed by Co3O4 derived of ZIF-67 as highly active cobalt source and Al2O3 decomposed from halloysite substrate as aluminum source. In addition, the corrosion resistance test showed that the CoAl2O4 composites retain crystalline stability, almost no color deviation in CIE chromatic system even after 1 M HCl leaching. Furthermore, the CoAl2O4/halloysite exhibited excellent thermal and suspension stability, which indicated it could be a promising candidate for ceramic glazes and water-borne coatings. These findings provide insight into a new strategy for the synthesis of clay mineral-based ceramic pigment.

Inorganic-organic hybrid pigments based on carminic acid and clay minerals

Recent researches on natural pigments stabilized by clay minerals: A review

Facile color regulation of organic/inorganic hybrid pigments combining with palygorskite and CoNi layered double hydroxides

Fabrication of multifunctional hybrid pigment for color cosmetics based on chitosan-modified palygorskite and sappanwood extract

Carminic Acid Stabilized with Aluminum-Magnesium Hydroxycarbonate as New Colorant Reducing Flammability of Polymer Composites

Advancing Chlorophyll Photostability: Dual Physicochemical Protection via Ce-Doped Hydrotalcite Organic-Inorganic Hybrid Pigments

Formation and Coloring Mechanism of Typical Aluminosilicate Clay Minerals for CoAl2O4 Hybrid Pigment Preparation

Preparation of Acid Red73 adsorbed on chitosan-modified sepiolite with SiO2 coating as a highly stable hybrid pigment

Preparation of Palygorskite hybrid iron oxide red pigment and its application in waterborne polyurethane composite coatings and ceramics

Synthesis of an Intensive Blue Pigment with Low Cobalt Content

Coordinated water stabilizes indigo-sepiolite hybrid pigments: Evidence from acid modification

A high-stability silica-clay composite: synthesis, characterization and combination with TiO2 as a novel photocatalyst for Azo dye.

Synthesis and characterization of iron oxides and their application as inorganic pigments in white paint

Novel fabrication of rod-like CoAl2O4/halloysite hybrid pigment derived from Co-MOF/nano-clay and mechanism exploration

Preparation of Hybrid Nanopigments with Excellent Environmental Stability, Antibacterial and Antioxidant Properties Based on Monascus Red and Sepiolite by One-Step Grinding Process

Facile mechanochemical fabrication of hybrid pigments with allochroic, antibacterial and superhydrophobic properties based on organo-palygorskite and curcumin

RESEARCH PROGRESS IN YELLOW PIGMENTS OF RARE EARTH

Fabrication of Eco-Friendly Betanin Hybrid Materials Based on Palygorskite and Halloysite

Novel environment friendly inorganic red pigments based on attapulgite

Non-iridescent Structurally Colored Pigments Based on CB@SiO 2 @TiO 2 Core-Bishell Nanospheres with Enhanced Color Stability and Excellent Photocatalytic Activity

Preparation and colloidal dispersion behaviors of silica sol doped with organic pigment