The (110) plane dominated FeSe 2 particle microspheres@N-doped carbon interweaved network structure for enhanced potassium storage

Zijie Mu,Zongyou Li,Yanjun Gao,Qingyi Song,Hanjiao Huang,Songjie Gan,Lidong Xing,Jianguo Zhang,Wei Wang,Qiyao Yu

DOI: https://doi.org/10.1016/j.jpowsour.2024.234119

IF: 9.2

2024-02-02

Journal of Power Sources

Abstract:Transition metal dichalcogenides (TMDs) have the potential to be a high-capacity anode material for potassium ion batteries (PIBs) due to their multielectron transfer, while their rapid capacity decay hinders the commercial application due to large-sized K + . Herein, we design a new strategy to synthesize the (110) plane dominated FeSe 2 particle microspheres coated by N-doped carbon (FeSe 2 @C). The (110) plane dominated FeSe 2 can better facilitate the storage of the large-sized K + , and the surface carbon can inhibit the overgrowth of solid electrolyte interphase (SEI) during cycling. In addition, the porous structure provides abundant channels for K + diffusion, benefiting the rate performance. More importantly, the FeSe 2 microparticles would break down into smaller nanoparticles and mix with carbon layer to form interweaved network after cycling, which could expose more active sites for K + redox and enhance the structure stability, thus improving the specific capacity and cycling stability. As an anode material, this unique structure delivers a high capacity (363.2 mA h g −1 at 0.2 A g −1 over 200 cycles) and remarkable rate capability (285.2 mAh g −1 at 20 A g −1 ) in PIBs. Impressively, the FeSe 2 @C anode achieves a remarkable long-term cyclability (0.013 % capacity decay per cycle over 1000 cycles at 2 A g −1 ).

energy & fuels,materials science, multidisciplinary,electrochemistry,chemistry, physical