Abstract:The demand for high-performance supercapacitors exceeds the capabilities of pristine carbon materials and traditional electrolytes. To address this gap, we prepared a petal-like multicyclic polycondensate precursor (PCDP) using Knoevenagel reaction and amine/aldehyde condensation between 3 -aminorhodanine and p -phthalaldehyde. The subsequent activation of PCDP by KOH and carbonization at various temperatures (600–900 °C) were employed to produce N/S-dual doped porous carbon (N/S-DDPCs) for use as electrode materials. For N/S-DDPC8 carbonized at 800 °C, the specific surface area measured as the highest at 2047 m 2 g −1 with a significant number of interconnected micro/mesoporous structures and higher N and S contents of 3.57 % and 2.31 %, respectively. Furthermore, Zn(CF 3 SO 3 ) 2 aqueous electrolyte was developed using dimethyl oxalate (DMO) to regulate and improve the electrochemical performance of the N/S-DDPCs while also providing better stability. In comparison to the conventional Zn(CF 3 SO 3 ) 2 electrolyte, the utilization of N/S-DDPC8 in DMO-regulated Zn(CF 3 SO 3 ) 2 electrolyte resulted in a noteworthy enhancement in energy density and power density, soaring to 36.4 Wh kg −1 from 11.7 Wh kg −1 and to 642 W kg −1 from 250 W kg −1 at a current density of 0.5 A g −1 , respectively. It is particularly noteworthy that N/S-DDPC8-DMO-D can maintain 100 % specific capacitance even after 10,000 cycles, demonstrating its high-level electrochemical consistency. In brief, the porous N/S-DDPCs and DMO-regulated electrolyte created in this study serve as a valuable guide for boosting the electrochemical performance of supercapacitors.

N, S, O Self-Doped Carbon Derived from Grapefruit Peel for High-Performance Supercapacitors

N, S Co-doped hierarchical porous carbon rods derived from protic salt: Facile synthesis for high energy density supercapacitors

Hydrangea-like N/O codoped porous carbons for high-energy supercapacitors

Highly Active N, O-doped Hierarchical Porous Carbons for High-Energy Supercapacitors

Highly N/O co-doped ultramicroporous carbons derived from nonporous metal-organic framework for high performance supercapacitors

Efficient conversion of biomass waste to N/O co-doped hierarchical porous carbon for high performance supercapacitors

Facile Preparation of Porous Carbons Derived from Orange Peel Via Basic Copper Carbonate Activation for Supercapacitors

Thiocyanogen-modulated N, S Co-doped lignin hierarchical porous carbons for high-performance aqueous supercapacitors

Self-doped (N/O/S) nanoarchitectonics of hierarchically porous carbon from palm flower for high-performance supercapacitors

N/O Co-doped Porous Carbon with Controllable Porosity Synthesized via an All-in-One Step Method for a High-Rate-Performance Supercapacitor

High-performance supercapacitors enabled by N/S dual-doped porous carbon and DMO-regulated electrolyte

Freestanding biomass‐derived and self‐doped carbon electrodes with high loading for high‐performance supercapacitors

Waste sugar solution polymer-derived N-doped carbon spheres with an ultrahigh specific surface area for superior performance supercapacitors

O and N co-doped porous carbon derived from crop wastes for high-stability all-solid-state symmetric supercapacitor

Naturally O-N-S co-doped carbon with multiscale pore architecture derived from lotus leaf stem for high-performance supercapacitors

Biomass derived N/O self-doped porous carbon for advanced supercapacitor electrodes

Biotemplating Preparation of N,O-codoped Hierarchically Porous Carbon for High-Performance Supercapacitors

Oxygen-Enriched Hierarchical Nanoporous Carbon Electrodes for Supercapacitors

From weed to N/O/S co-doped honeycomb-like porous carbon for high-performance supercapacitors: a facile and friendly one-step carbonization

Boosting the capacitive performance by constructing O, N co-doped hierarchical porous structure in carbon for supercapacitor

Porous Carbon Electrode from Starch Soluble for Realizing High‐Performance Supercapacitor