Two-Step Chemical Vapor Deposition-Synthesized Lead-Free All-Inorganic Cs 3 Sb 2 Br 9 Perovskite Microplates for Optoelectronic Applications

Sujit Kumer Shil,Fei Wang,Kingsley O. Egbo,Zhengxun Lai,Ying Wang,Yunpeng Wang,Dongxu Zhao,Sai-Wing Tsang,Johnny C. Ho,Kin Man Yu

DOI: https://doi.org/10.1021/acsami.1c07839

2021-07-21

Abstract:Lead-based halide perovskites (APbX3, where A = organic or inorganic cation, X = Cl, Br, I) are suitable materials for many optoelectronic devices due to their many attractive properties. However, the concern of lead toxicity and the poor ambient and operational stability of the organic cation group greatly limit their practical utilization. Therefore, there has recently been great interest in lead-free, environment-friendly all-inorganic halide perovskites (IHPs). Sb and Sn are common species suggested to replace Pb for Pb-free IHPs. However, the large difference in the melting points of the precursor materials (e.g., CsBr and SbBr3 precursors for Cs3Sb2Br9) makes the chemical vapor deposition (CVD) growth of high-quality Pb-free IHPs a very challenging task. In this work, we developed a two-step CVD method to overcome this challenge and successfully synthesized Pb-free Cs3Sb2Br9 perovskite microplates. Cs3Sb2Br9 microplates ∼25 μm in size with the exciton absorption peak at ∼2.8 eV and a band gap of ∼2.85 eV were obtained. The microplates have a smooth hexagonal morphology and show a large Stokes shift of ∼450 meV and exciton binding energy of ∼200 meV. To demonstrate the applications of these microplates in optoelectronics, simple photoconductive devices were fabricated. These photodetectors exhibit a current on/off ratio of 2.36 × 102, a responsivity of 36.9 mA/W, and a detectivity of 1.0 × 1010 Jones with a fast response of rise and decay time of 61.5 and 24 ms, respectively, upon 450 nm photon irradiation. Finally, the Cs3Sb2Br9 microplates also show good stability in ambient air without encapsulation. These results demonstrate that the 2-step CVD process is an effective approach to synthesize high-quality all-inorganic lead-free Cs3Sb2Br9 perovskite microplates that have the potential for future high-performance optoelectronic device applications.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c07839.Schematic illustration of the two-step chemical vapor deposition synthesis of Cs3Sb2Br9 perovskite microplates; XRD patterns after each step of Cs3Sb2Br9 perovskite microplate synthesis; XRF spectrum of as-grown sample before annealing; optical images of Cs3Sb2Br9 microplates on different substrates; AFM images and XRF spectrum of Cs3Sb2Br9 microplates; SEM image and EDX spectrum of a single 3D structure; ellipsometric experimental and simulated spectra of Ψ and Δ for Cs3Sb2Br9 perovskite microplates; experimental data and modeled plot for ε2 along with different T–L oscillators of Cs3Sb2Br9 microplates; best fit parameters for the Tauc–Lorentz oscillators; UV–vis absorption spectrum; incident power density dependent photocurrent of the device; power-dependent photocurrent plot and the corresponding power law fitted curve; dark I–V plot of the device used to calculate trap state density; comparison of the XRD patterns of Cs3Sb2Br9 microplates between fresh and after storage in ambient; rocking curve for (201) plane of Cs3Sb2Br9 microplates fresh and after storage for 2 months in ambient condition; comparison of the photoresponse of the photodetector between fresh and after 2 months storage in ambient condition (PDF)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology