Improved shape stability and ceramifiable properties of ceramifiable polyethylene composites by crystallization reaction

Jiapei Shen,Qing Sun,Lang Li,Jian Zhang,Jiawei Sheng

DOI: https://doi.org/10.1016/j.polymdegradstab.2022.109965

IF: 5.204

2022-06-01

Polymer Degradation and Stability

Abstract:Wollastonite fiber (WF) was added to further improve shape stability and ceramifiable properties of polyethylene (PE)/ mica/ phosphate glass frits (PGF) composites. To evaluate shape stability property, the surface cracking of ceramic-like residues obtained by calcining at different temperatures were observed, and dimensional variation and self-supporting properties of the residues were measured. The ceramifiable properties (flexural strength and apparent porosity) of the PE composites were also investigated. Results showed that the addition of WF reduced surface cracking effectively, improved dimensional stability and self-supporting properties. Furthermore, at high temperatures, the flexural strength of the PE composites was enhanced by incorporation of WF, accompanying with the reduction of porosity. X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) were used to analyze the effect of WF on the performance of the PE composites. Results showed that there was a novel crystalline phase hydroxyapatite (HAP) was formed within the residues. During the heat treatment process, WF acted as the promoter to participate in a crystallization reaction with molten phosphate glassy phase by the way of ion diffusion to generate the HAP. The crystallization thermodynamics demonstrated that the reaction could occur spontaneously above 873 K. Crystallization reaction improved the crystallinity, which was beneficial to enhance the flexural strength. Moreover, crystallization kinetic analysis was investigated. The results indicated that the growth of crystal HAP was promoted with the increase of temperature and the flow of glassy phase was limited, which improved the shape stability. Therefore, it was inferred that crystallization reaction played an important role in the improvement of the shape stability and ceramifiable properties of PE composite simultaneously.

polymer science