Abstract:With increasing environmental requirements, biodegradable polymers have received widespread attention. Herein, we synthesized a series of poly(butylene diglycolate)s (PBDs), which was a novel biodegradable homopolyester, with number-average molecular weight (M n) values between 13 and 97 K g·mol–1. The effects of M n on the thermal and tensile properties of PBDs were comprehensively investigated. The glass transition temperature (T g), melting temperature (T m), and temperature of 5% weight loss (T d,5%) of PBDs were found to be approximately −26.4, 64.0, and 336 °C, respectively. PBD with 31 K g·mol–1 exhibits a brittle fracture feature, while obvious yielding behavior occurs when the M n of PBD is higher than 45 K g·mol–1. Besides, PBD achieves stable mechanical properties when M n reaches 51 K g·mol–1, with the elastic modulus, tensile strength, and elongation at break of 285, 27.1 MPa, and 290%, respectively, superior to those of linear low-density polyethylene (LLDPE). Furthermore, the crystal structures of PBD were recorded by WAXD and POM. The spherulites were observed after isothermal crystallization of PBD in a wide temperature range, and the maximum nucleation density was obtained after annealing at 20 °C. Significant hydrolysis of PBD in both buffer solution and artificial seawater was confirmed by monitoring the changes in residual weight, intrinsic viscosity, surface morphology, crystallinity, and chemical composition. Finally, PBD exhibits considerable biodegradability under composting and freshwater environments, with the residual weight reducing to 49.2 and 94.7% after 35 days, respectively. Due to the balanced mechanical and barrier properties and biodegradability, PBD has potential application prospects in packaging materials.

Synthesis, Physical Properties, and Functionalization of Biobased Unsaturated Polyesters Derived from Cis-2-butene-1,4-diol

Synthesis And Properties Of Long Chain Polyesters From Biobased 1,5-Pentanediol And Aliphatic Alpha,Omega-Diacids With 10-16 Carbon Atoms

High Molecular Weight Polyesters Derived from Biobased 1,5-Pentanediol and a Variety of Aliphatic Diacids: Synthesis, Characterization, and Thermo-Mechanical Properties

Biobased 1,5-Pentanediol Derived Aliphatic-Aromatic Copolyesters: Synthesis and Thermo-Mechanical Properties of Poly(pentylene Succinate-Co-terephthalate)s and Poly(pentylene Adipate-Co-terephthalate)s

Synthesis and Thermomechanical and Rheological Properties of Biodegradable Long-Chain Branched Poly(Butylene Succinate-Co-Butylene Terephthalate) Copolyesters

Cleavable Polybutadiene Rubber: A Versatile Precursor to Hydroxyl-Terminated or Multi-Hydroxyl Polybutadiene and Polyethylene

Biobased unsaturated polyesters containing trans-2-butene-1,4 -diol and various dicarboxylic acids: Synthesis, characterization, and thermo-mechanical properties

Modification of Biodegradable Poly(Butylene Carbonate) by Biobased cis -2-Butene-1,4-Diol

Synthesis of Aromatic Polyesters with Pendent Carboxyl Groups from Diphenolic Acid, Bisphenol a and Isophthaloyl Chloride by Interfacial Polycondensation

Trans -2-Butene-1,4-Diol as an Olefinic Building Block to Prepare Biobased Unsaturated Copolyesters with High Molecular Weight: Synthesis, Characterization, and Physical Properties

High Molecular Weight Soybean Oil-based Polyesters through Carboxyl-ester Transesterification

Catalyst-free synthesis of polyesters via conventional melt polycondensation

Aliphatic Polyester Materials from Renewable 2,3-Butanediol

Synthesis of linear functionalized polyesters by controlled atom transfer radical polyaddition reactions

Synthesis and Post-Functionalization of Poly(conjugated ester)s Based on 3-Methylene-1,5-dioxepan-2-one

Aliphatic polyesters based on 1,4-butanediol and even numbered C4 - C20 dicarboxylic acids - synthesis and properties including after surface treatment by VUV photo-oxidation

Synthesis and Characterization of Diastereoisomeric Polyesters Derived from Bisphenols Bearing Vicinal Trifluoromethyl Groups

Chemical Synthesis of Functional Poly(4-hydroxybutyrate) with Controlled Degradation Via Intramolecular Cyclization

Preparation and performance exploration of 2,5‐furandicarboxylic acid‐based copolyester bioplastics: Controlling thermal properties, tensile properties, and surface hydrophilicity through composition

Study on the Synthesis and Properties of Biodegradable Poly(butylene diglycolate) Polyester

Biobased Bifunctional Monomers toward Functionalizable Polycarbonates and Poly(cyclic olefin)s with Tunable Properties