Abstract:A robust nanocasting approach is demonstrated to synthesize encapsulated nanoparticles in metal oxides. First, colloidal nanoparticles are encapsulated in a porous polymer matrix. Then, metal oxide precursor is infiltrated, and materials are calcined to form a porous metal oxide network. Various combinations of nanoparticles encapsulated in metal oxide materials can be synthesized, and their surface area and porosity can be tuned using this method. Encapsulation of metal nanoparticles within oxide materials has been shown as an effective strategy to improve activity, selectivity, and stability in several catalytic applications. Several approaches have been proposed to encapsulate nanoparticles, such as forming core‐shell structures, growing ordered structures (zeolites or metal‐organic frameworks) on nanoparticles, or directly depositing support materials on nanoparticles. Here, a general nanocasting method is demonstrated that can produce diverse encapsulated metal@oxide structures with different compositions (Pt, Pd, Rh) and multiple types of oxides (Al2O3, Al2O3‐CeO2, ZrO2, ZnZrOx, In2O3, Mn2O3, TiO2) while controlling the size and dispersion of nanoparticles and the porous structure of the oxide. Metal@polymer structures are first prepared, and then the oxide precursor is infiltrated into such structures and the resulting material is calcined to form the metal@oxide structures. Most Pt@oxides catalysts show similar catalytic activity, demonstrating the availability of surface Pt sites in the encapsulated structures. However, the Pt@Mn2O3 sample showed much higher CO oxidation activity, while also being stable under aging conditions. This work demonstrated a robust nanocasting method to synthesize metal@oxide structures, which can be utilized in catalysis to finely tune metal‐oxide interfaces.

Rapid room-temperature synthesis of a porphyrinic MOF for encapsulating metal nanoparticles

Structuring Metal-Organic Framework Materials into Hierarchically Porous Composites Through One-Pot Fabrication Strategy

General Immobilization of Ultrafine Alloyed Nanoparticles within Metal–Organic Frameworks with High Loadings for Advanced Synergetic Catalysis

Synthesis, Morphology Control, and Properties of Porous Metal–organic Coordination Polymers

Incorporating metal nanoparticles in porous materials via selective heating effect using microwave

A general strategy for overcoming the trade-off between ultrasmall size and high loading of MOF-derived metal nanoparticles by millisecond pyrolysis

A Facile Route to Metal-Oxide Nanocrystals by Direct Pyrolysis of Metal-Organic Frameworks

Regulation of Electron Density in Pt Nanoparticles Via Bimetallic Metal-Organic Frameworks for Enhancing Photothermal Catalysis of Toluene Decomposition

Imparting Functionality to a Metal–organic Framework Material by Controlled Nanoparticle Encapsulation

Synthesis of Ultrafine and Highly Dispersed Metal Nanoparticles Confined in a Thioether-Containing Covalent Organic Framework and Their Catalytic Applications

A General Approach for Metal Nanoparticle Encapsulation Within Porous Oxides

Ferrocenyl metal-organic framework hollow microspheres for in situ loading palladium nanoparticles as a heterogeneous catalyst.

Microplasma Electrochemistry (MIPEC) Strategy for Accelerating the Synthesis of Metal Organic Frameworks at Room Temperature

Regulating the spatial distribution of metal nanoparticles within metal-organic frameworks to enhance catalytic efficiency

Metal Organic Frameworks As Robust Host of Palladium Nanoparticles in Heterogeneous Catalysis: Synthesis, Application, and Prospect

In situ biosynthesis of ultrafine metal nanoparticles within a metal-organic framework for efficient heterogeneous catalysis

Integration of Pd nanoparticles with engineered pore walls in MOFs for enhanced catalysis

Dynamic Bond-Directed Synthesis of Stable Mesoporous Metal-Organic Frameworks under Room Temperature

Immobilizing Metal Nanoparticles on Hierarchically Porous Organic Cages with Size Control for Enhanced Catalysis

Encapsulation of C-N-decorated Metal Sub-Nanoclusters/single Atoms into a Metal-Organic Framework for Highly Efficient Catalysis.

General Incorporation of Diverse Components Inside Metal-Organic Framework Thin Films at Room Temperature.