Photocatalytic degradation of sulfamonomethoxine by mesoporous phosphorus-doped titania under simulated solar light irradiation

Jiang Li,Qi Su,Huayu Yuan,Lin Zhang,Li'an Hou,Yuehu Wang,Baojun Liu,Bing Wang,Yancheng Li

DOI: https://doi.org/10.1016/j.chemosphere.2021.131553

IF: 8.8

2021-12-01

Chemosphere

Abstract:<p>Photocatalytic degradation of sulfamonomethoxine (SMM) by mesoporous phosphorus-doped TiO₂ (P–TiO₂) was studied under simulated solar light irradiation. The morphological structure and chemical composition of P–TiO₂ were analyzed by XRD, SEM, HRTEM, BET, XPS and FTIR. Using the central composite design (CCD) of response surface methodology (RSM), the degradation of SMM was investigated with a range of antibiotic concentrations (4–8 mg L⁻¹), catalyst dosages (400–900 mg L⁻¹), P doping amounts (5–15 wt %) and irradiation time (90–150 min). The Ti–O–P bond formed during the calcination of TiO₂, thereby generating plate-like P–TiO₂, where P was uniformly distributed. Phosphorus doping can stabilize anatase TiO₂, which has a larger specific surface area and a lower average particle and pore size than bare TiO₂. The result obtained from the RSM model showed a significant correlation between the predicted values and the experimental results of SMM degradation (P &lt; 0.05). Under the optimal experimental conditions (antibiotic concentration = 6 mg/L, catalyst dosage = 800 mg/L, P doping = 5 wt% and irradiation time = 90 min), the degradation rate of SMM was 99.51%, and the TOC was 50%. Toxicity showed a considerable reduction towards <em>Vibrio</em>-<em>qinghaiensis</em> sp.<em>-</em>Q67 after SMM photocatalytic degradation. Through free radical capture experiments, LC-MS detection and DFT calculations, the possible photocatalytic degradation mechanism of SMM using P–TiO₂ as the catalyst was revealed.</p>

environmental sciences