Green synthesis of 3D core-shell SnS 2 /SnS-Cd 0.5 Zn 0.5 S multi-heterojunction for efficient photocatalytic H 2 evolution

Haitao Zhao,Baohua Zhao,Heyuan Liu,Xiyou Li

DOI: https://doi.org/10.1039/d3dt03533f

IF: 4

2023-11-30

Dalton Transactions

Abstract:Low charge carrier's separation efficiency is one of the key factors restricting photocatalytic hydrogen evolution performance. It is an effective strategy to build heterojunctions to steer charge migration. Herein, a series of x-SnS 2 /SnS-Cd 0.5 Zn 0.5 S (x-SS-CZS) nanospheres composites with varying mass ratios of SnS 2 /SnS (SS) were prepared through in-situ hydrothermal synthesis. Moreover, XRD, TEM, and XPS were used to characterize the creation of 3D core-shell SS-CZS multi-heterojunction composite. The 5-SS-CZS heterojunction composite with 5 wt% content of SS exhibits remarkable hydrogen evolution rate of 168.85 mmol g -1 h -1 , which is 5.4 times higher than that of pristine twin CZS (31.08 mmol g -1 h -1 ) and 1.9 times higher than that of 5-SnS 2 -CZS (88.21 mmol g -1 h -1 ). Furthermore, composite catalyst shows excellent photostability after four cycle reactions under visible light illumination. The apparent quantum yield at λ = 420 nm can reach up to 24.78%. The excellent hydrogen evolution performance of 5-SS-CZS nanospheres is ascribed to the following factors: (1) Core-shell catalyst with broad spectral absorption improves light utilization efficiency; (2) hybrid material with large surface area provides more active sites and shows the highest H 2 activity; (3) Multi-heterojunction composite extends the lifetime of photoinduced carriers and accelerates charge separation and migration; (4) SS as a hole trapping agent enhances photocatalytic stability performance. This work proposes a possible photocatlytic mechanism, while also provides a novel approach for the synthesis of highly active and stable photocatalysts.

chemistry, inorganic & nuclear