Abstract:A short lifetime of perovskite photovoltaics, with respect to extrinsic and intrinsic instability, originates from the decomposition of function‐layer materials, the failure of heterointerfaces, and the degradation of optoelectronic performance against multiple stressors. Stabilizing strategies from material processing, film formation, interface strengthening, structure designing, and device encapsulation can systematically improve the durability of perovskite photovoltaics and facilitate their commercialization. Over the last decade, perovskite solar cells (PSCs) have drawn extensive attention owing to their high power conversion efficiency (single junction: 26.1%, perovskite/silicon tandem: 33.9%) and low fabrication cost. However, the short lifespan of PSCs with initial efficiency still blocks their practical applications. This operational instability may originate from the intrinsic and extrinsic degradation of materials or devices. Although the lifetime of PSCs has been prolonged through component, crystal, defect, interface, encapsulation engineering, and so on, the systematic analysis of failure regularity for PSCs from the perspective of materials and devices against multiple operating stressors is indispensable. In this review, we start with elaboration of the predominant degradation pathways and mechanism for PSCs under working stressors. Then the strategies for improving long‐term durability with respect to fundamental materials, interface designs, and device encapsulation have been summarized. Meanwhile, the key results have been discussed to understand the limitation of assessing PSCs stability, and the potential applications in indoor photovoltaics and wearable electronics are demonstrated. Finally, promising proposals, encompassing material processing, film formation, interface strengthening, structure designing, and device encapsulation, are provided to improve the operational stability of PSCs and promote their commercialization.

Understanding degradation mechanisms of perovskite solar cells due to electrochemical metallization effect

Mechanisms and Suppression of Photoinduced Degradation in Perovskite Solar Cells

Comprehensive Understanding of Heat-Induced Degradation of Triple-Cation Mixed Halide Perovskite for a Robust Solar Cell

Unraveling the Degradation Mechanisms of Perovskite Solar Cells under Mechanical Tensile Loads

Progress in research on the stability of organometal perovskite solar cells

Interfacial Degradation of Planar Lead Halide Perovskite Solar Cells

Efficient and Stable of Perovskite Solar Cells

Stability of Perovskite Solar Cells: Degradation Mechanisms and Remedies

Inhomogeneous Degradation in Metal Halide Perovskites

An overview of the decompositions in organo-metal halide perovskites and shielding with 2-dimensional perovskites

In‐situ characterization for understanding the degradation in perovskite solar cells

Synergetic Acceleration on the Degradation of Flexible Perovskite Solar Cells under Light and Stress Cooperation

Stability Improvement of Perovskite Solar Cells by Compositional and Interfacial Engineering

Impeded Degradation of Perovskite Solar Cells Via the Dual Interfacial Modification of Siloxane

Unveiling and overcoming the interfacial degradation between CuSCN and metal electrodes in perovskite solar cells

Towards Long-Term Stable Perovskite Solar Cells: Degradation Mechanisms and Stabilization Techniques

Towards operation‐stabilizing perovskite solar cells: Fundamental materials, device designs, and commercial applications

Measuring metal halide perovskite single cell degradation consistent with module-based conditions

Degradation pathways in perovskite solar cells and how to meet international standards

Strategies for Improving Efficiency and Stability of Perovskite Solar Cells

Interface Engineering for Highly Efficient and Stable Perovskite Solar Cells