TiB4 and SrB8 monolayers: high capacity and zero strain-like anode materials for Li/Na/K/Ca ion batteries
Yunxin Wang,Sisi Liang,Juncheng Tian,Huixian Duan,Ying Lv,Lijia Wan,Chunlai Huang,Musheng Wu,C. Y. Ouyang,Junping Hu
DOI: https://doi.org/10.1039/d3cp05287g
IF: 3.3
2024-01-06
Physical Chemistry Chemical Physics
Abstract:Storage capacity, average open circuit voltage (OCV), diffusion barrier, and lattice parameter changes, etc. are key indicators of whether a material would be suitable for use as a Li-ion or non-Li-ion batteries (LIBs or NLIBs) anode. The rapid development of 2D materials over the past few decades has opened up new possibilities for these metrics. Using first-principles calculations, we prove that two 2D materials, TiB4 and SrB8, have excellent performance in the above metrics when used as anodes for LIBs or NLIBs. As detailed, TiB4 has Li\Na\K\Ca storage capacity of 588mAh/g, 588mAh/g, 588mAh/g, and 1176mAh/g, respectively and SrB8 has Li\Na\K\Ca storage capacity of 308mAh/g, 308mAh/g, 462 mAh/g, and 616 mAh/g, respectively, and shows good electrical conductivity whether existing Li, Na, K or Ca adsorption or not. The diffusion barriers on both surfaces are low, indicating good rate performance. The average OCV is also very low. In particular, the lattice parameters of the two materials change very little during the embedding of Li\Na\K\Ca. For Ti9B36 the corresponding values are about 0.37% (Li), 0.33% (Na), 0.64% (K) and 0.03% (Ca), for Sr8B64 the corresponding values are about 0.70% (Li), 0.16% (Na), 0.13% (K) and 0.004% (Ca), which implies zero strain-like character and great cycling performance. All the above results show that TiB4 and SrB8 monolayers are very promising Li\Na\K\Ca ion batteries anodes.
chemistry, physical,physics, atomic, molecular & chemical