Fabrication of 2D/3D hierarchical PBA and derivative electrocatalysts for overall water splitting

Li Shen,Qing Zhang,Juan Luo,Hong Chuan Fu,Xiao Hui Chen,Li Li Wu,Hong Qun Luo,Nian Bing Li
DOI: https://doi.org/10.1016/j.apsusc.2021.149360
IF: 6.7
2021-06-01
Applied Surface Science
Abstract:<p>Assembling a hierarchical well-defined Prussian blue analogues (PBA) construction is a useful way to take earth-abundant elements into application toward hydrogen evolution reaction (HER) and oxygen evolution reaction (OER). Herein, we report a unique strategy for in-situ grafting three-dimensional (3D) MnFe-PBA cubes on the top of two-dimensional (2D) MnO<sub>2</sub> nanosheet arrays (<sub>2</sub>) via a facile two-step hydrothermal method with the participation of Ni foam (NF). After experiencing low-temperature pyrolysis in NH<sub>3</sub>/Ar atmosphere, the above catalysts are transformed into metal-nitride derivatives (N-FeMnNi). Remarkably, when operated in 1.0 M KOH aqueous solution, the as-obtained <sub>2</sub>-150/30 (where 150 and 30 represent the hydrothermal temperature (℃) and the concentration of K<sub>3</sub>Fe(CN)<sub>6</sub> (mM) for preparation, respectively) shows the most outstanding OER activity, with an overpotential of 238 mV at 10 mA cm<sup>-2</sup>. Moreover, N-FeMnNi-130/10 requires an overpotential of 101 mV to reach 10 mA cm<sup>-2</sup> for HER. As a result, the two samples are organized to establish a two-electrode cell, with a voltage of only 1.60 V needed to reach 10 mA cm<sup>-2</sup>. Meanwhile, it can stably work for 30 h without obvious current attenuation. This work provides a brand new perspective for the design of PBA electrocatalysts towards high-efficiency overall water splitting.</p>
chemistry, physical,physics, applied, condensed matter,materials science, coatings & films
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to develop highly efficient and low - cost electrocatalysts for overall water splitting (i.e., simultaneous hydrogen evolution reaction (HER) and oxygen evolution reaction (OER)). Specifically, by constructing 2D/3D hierarchical Prussian blue analogues (PBA) and their derived metal nitride composites, the authors aim to improve the catalytic performance of the catalysts under alkaline conditions, especially to reduce the overpotential, improve the reaction kinetics, and enhance the stability of the materials. The ultimate goal of these catalysts is to achieve efficient energy conversion and storage in the overall water - splitting process, so as to replace traditional high - cost noble - metal catalysts such as platinum (Pt) and iridium oxide (IrO₂). ### Main research contents: 1. **Catalyst design and synthesis**: - A 2D MnO₂ nanosheet array was prepared on nickel foam (NF) by a two - step hydrothermal method, and 3D MnFe - PBA cubes were in - situ grown on top of it to form the PBA@MnO₂ composite. - After heat treatment in a low - temperature ammonia/argon atmosphere, PBA@MnO₂ was converted into the metal nitride derivative N - FeMnNi. 2. **Catalyst characterization**: - Techniques such as scanning electron microscopy (SEM), transmission electron microscopy (TEM), X - ray diffraction (XRD), and X - ray photoelectron spectroscopy (XPS) were used to characterize the morphology, structure, and composition of the catalysts in detail. 3. **Electrochemical performance testing**: - In a 1.0 M KOH solution, the catalytic activity and stability of PBA@MnO₂ and N - FeMnNi in OER and HER were evaluated by methods such as linear sweep voltammetry (LSV), Tafel slope, double - layer capacitance (Cdl), and electrochemical impedance spectroscopy (EIS). ### Key findings: - **OER performance**: - PBA@MnO₂ - 150/30 exhibits the lowest overpotential (238 mV) at a current density of 10 mA/cm², much lower than that of commercial RuO₂ (259 mV). - Through EIS testing, it was found that PBA@MnO₂ - 150/30 has the lowest charge - transfer resistance (Rct), indicating its excellent conductivity and fast OER kinetics. - **HER performance**: - N - FeMnNi - 130/10 exhibits the lowest overpotential (101 mV) at a current density of 10 mA/cm², better than that of untreated PBA@MnO₂ and MnO₂. - N - FeMnNi - 130/10 exhibits a lower Tafel slope (79.7 mV dec⁻¹) during the HER process, indicating its good catalytic kinetics. - **Overall water - splitting performance**: - When PBA@MnO₂ - 150/30 and N - FeMnNi - 130/10 are combined into a two - electrode system, a current density of 10 mA/cm² can be achieved with only a voltage of 1.60 V, and stable performance is exhibited within 30 hours. ### Conclusion: This study has successfully developed an efficient and low - cost 2D/3D hierarchical electrocatalyst for overall water splitting. By optimizing the morphology and composition of the catalyst, its catalytic performance and stability in OER and HER have been significantly improved, providing new ideas for the development of new non - noble - metal - based electrocatalysts.