Transesterification catalyzed via ferric chloride for fabricating Poly(lactic acid)/Poly(butylene adipate-co-terephthalate) blends with ultra-fast degradation and high toughness

Xiaolong Li,Shang Gong,Le Yang,Xiaosong Xia,Changkai Linghu,Jun Wang,Zhu Luo

DOI: https://doi.org/10.1016/j.polymer.2021.123927

IF: 4.6

2021-07-01

Polymer

Abstract:<p>The low degradation velocity of poly(lactic acid) (PLA)/poly(butylene adipate-<em>co</em>-terephthalate) (PBAT) leads to an excessive accumulation of waste PLA/PBAT, which is not conducive to environmental protection and sustainable development. In this work, the rapidly degradable PLA/PBAT/FeCl₃ blends were successfully prepared by adding a small amount of ferric chloride (FeCl₃) using the melt blending method. The materials showed appropriate mechanical strength while maintained a high degradation rate. For P/P-1 with 0.1 phr FeCl₃ added, the degradation rate was 15.27 times higher than that of pure PLA and 4.19 times for P/P, the impact strength and elongation at break were 1.76 times and 1.09 times higher than that of PLA, respectively. During degradation, FeCl₃ reacted preferentially with the ester bond of the PBAT chain close to the benzene ring in the P/Ps blends, followed by the ester bond on the aliphatic chain. The P/P-1 shows promising potential value in the application of rapidly degrading solid waste treatment and biomedical material (artificial ureter).</p>

polymer science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the slow degradation rate of the blend of polylactic acid (PLA) and poly(adipic acid - co - terephthalic acid) butylene ester (PBAT). Specifically:

1. **Environmental issues**: Due to the slow degradation rate of the PLA/PBAT blend, too much waste accumulates in the environment, which is not conducive to environmental protection and sustainable development.
2. **Balance between mechanical properties and degradability**: Although the toughness of the PLA/PBAT blend can be improved by adding PBAT, its degradation efficiency is still very low and it is difficult to meet the needs of daily life.

To solve these problems, the researchers proposed a method of adding a small amount of ferric chloride (FeCl₃) to the PLA/PBAT blend by melt - blending to achieve rapid degradation while maintaining good mechanical properties. The experimental results show that this method not only significantly improves the degradation rate of the material but also improves its mechanical properties.

### Key improvement points:
- **Degradation rate**: The degradation rate of the P/P - 1 sample containing 0.1 phr FeCl₃ in an alkaline solution is 15.27 times higher than that of pure PLA and 4.19 times higher than that of P/P.
- **Mechanical properties**: The impact strength and elongation at break of P/P - 1 are 1.76 times and 1.09 times higher than those of pure PLA, respectively.

### Degradation mechanism:
FeCl₃ preferentially reacts with the ester bond near the benzene ring in the PBAT chain, and then attacks the ester bond on the aliphatic chain. This selective degradation mechanism makes the partially degraded PBAT molecular chain toughen the PLA.

### Potential applications:
This research not only provides new ideas for the treatment of rapidly degradable solid waste but also shows potential application value in the biomedical field (such as artificial ureters).

In conclusion, this paper aims to develop a PLA/PBAT blend with both rapid degradation and good mechanical properties by introducing the FeCl₃ catalyst to meet the current challenges in plastic waste treatment.