Frontal polymerization for UV‐ and thermally initiated EPON 826 resin

Gabrielle Esposito,Gyaneshwar Tandon,Andrew Abbott,Dennis Butcher,Hilmar Koerner

DOI: https://doi.org/10.1002/pen.26879

2024-08-19

Polymer Engineering & Science

Abstract:Real time frontal polymerization of EPON 826, as well as images of resin printed and frontally cured with UV initiation. Selected graphs include change in front velocity with initiator content (left), viscosity changes with increasing time from preparation (center), and tan(δ) of frontally cured samples with increasing initiator content (right). Frontal polymerization has great potential in complementing additive manufacturing processes such as direct ink writing as a continuous cure synchronized to the printing speed can overcome issues such as sagging. To study the incorporation of frontal polymerization into a potential printing process, a frontally polymerizable DGEBA epoxy resin has been developed for both UV and thermal initiation. Through frontal polymerization alone, full conversion is observed with a starting glass transition of 150°C for both initiation methods. Resulting thermal behavior is shown to have little dependence on either initiation irradiance or temperature utilized and much greater dependence on initiator concentration in the resin. Mechanical behavior is maximized by varying initiator concentration and cure conditions achieving tensile stress of 75 MPa and K1C of 1.2 MPa‐m1/2. Shelf stability of the resin proves promising with no viscosity change after 12 weeks of room temperature storage. Future studies will concern adapting the resin for both direct ink writing and continuous fiber additive manufacturing applications. Highlights Frontal polymerization of EPON 826 using RICFP Utilized a tetrakis borate containing diaryliodonium cationic initiator Stable and polymerizable after 12 weeks Resin printed and frontally cured using UV initiation

engineering, chemical,polymer science