Abstract:The use of coatings to protect metals from corrosion is currently a common practice. In this study, a double bond-terminated waterborne polyurethane prepolymer was firstly synthesized from polycaprolactone polyol, toluene diisocyanate, dimethylolpropionic acid and hydroxyethyl methacrylate. Then, waterborne polyurethane prepolymer was modified with styrene, butyl acrylate, glycidyl methacrylate, and dodecafluoroheptyl methacrylate though soap-free emulsion polymerization method in order to obtain the crosslinked fluorinated acrylate modified waterborne polyurethane (CFWPUA). The CFWPUA emulsion was used as the matrix resin to prepare the coating with a bar coater, which possesses the characteristics of external hydrophobic surface constructed by long fluorinated side-chains and internal double cross-linking system. The results of infrared spectrum analysis proved the successful synthesis of modified waterborne polyurethane. The energy-dispersive X-ray spectroscopy results showed that the long fluorine side-chains partially migrate to the surface of the coating during the curing process, which leads to the occurrence of fluorine enrichment on the surface. When the glycidyl methacrylate content is 5 wt% and the dodecafluoroheptyl methacrylate content is 7.5 wt%, the water absorption rate of the membrane reduces to 7.9%, the water contact angle of the coating reaches 102.5°, and the gel content is 91%, which proved the successful construction of the double cross-linking system and prevents the penetration of water molecules. The pencil hardness of CFWPUA coating can reach 3H and flexibility and adhesion properties are at the highest level. Most importantly, in the electrochemical impedance spectroscopy test, the modified waterborne polyurethane coating effectively protects Q235 metal substrate from corrosion in the 3.5 wt% NaCl solution, the impedance modulus of CFWPUA coating could be maintained at about 107 Ω·cm2 for a long time, the resistance of CFWPUA coating slowly decreased from 2.124 × 107 Ω·cm2 to 9.605 × 106 Ω·cm2 within 10 days of immersion, two-time constant was generated after 12 days of immersion, which is slightly superior compare to commercial waterborne fluorocarbon coating. The modified waterborne polyurethane coating prepared here shows a potential practical application in the field of metal anti-corrosion.

Water-borne ultrathin intumescent fireproof and anticorrosive double-function coating for steel structure and preparation method thereof

Water-based intumescent fire resistance coating containing organic-modified glass fiber for steel structure

Steel structure fireproof anticorrosion function integrated coating and preparing method thereof

Study on Water Based Ultra-thin Fire Resistive Coating for Steel Structure and the Fire Resistance Test

Biomimetic construction of green, fire-proof and super-hydrophobic multifunctionality-integrated coatings via one-step spraying method for steel structures

Facile and effective construction of superhydrophobic, multi-functional and durable coatings on steel structure

One-Step Spraying Strategy for Fabricating Bioinspired, Graphene-Based, and Multifunctional-Integrated Coatings on Structural Steel with Good Water Repellency, Fireproofing, Anticorrosion, and Durability

Preparation and Properties of Waterborne Acrylic-Modified Epoxy Phosphate Resin and Its Coating

A promising strategy for enhancing fire resistance of steel structure: a composite thermoplastic polyurethane sheet adhered to steel plate

Preparation and characteristics of crosslinked fluorinated acrylate modified waterborne polyurethane for metal protection coating

Preparation of self-healing superhydrophobic polyacrylate coatings based on silica matrix-microcapsules containing corrosion inhibitor for long-term corrosion protection

A Cost-Effective Method for Preparing Anti-Corrosive and Fireproof Super Hydrophobic Coating

Eco-friendly waterborne superhydrophobic/superoleophilic FEVE composite coating with prolonged mechanochemical and anti-scaling properties

Preparation and Properties of Anti-corrosion Multifunctional Fluorocarbon Coatings

Fluorinated epoxy based superhydrophobic coating with robust self-healing and anticorrosive performances

Preparation of Superhydrophobic Materials and Establishment of Anticorrosive Coatings on the Tinplate Substrate by Alkylation of Graphene Oxide

Hybrid superamphiphobic anti-corrosion coating with integrated functionalities of liquid repellency, self-cleaning, and anti-icing

Fireproof and high temperature resistant coating

Novel Environmentally Friendly Waterborne Epoxy Coating with Long-Term Antiscaling and Anticorrosion Properties

Fabrication of self-healable superhydrophobic polyurethane coating based on functional CeO 2 nanoparticles for long-term anti-corrosion application

Hydrophobic Modification of Pentaerythritol and Its Application in Fire-Retardant Coatings for Steel Structures