Abstract:A Cu-doped Fe 2 O 3 /g-C 3 N 4 composite, synthesized via a straightforward hydrothermal process with controlled morphologies, represents a significant advancement in supercapacitor electrode materials.
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to improve the performance of supercapacitors. Specifically, the research aims to improve the electrochemical performance of supercapacitor electrode materials by synthesizing and characterizing a new type of copper - doped iron oxide / graphitic carbon nitride (Cu - Fe₂O₃/g - C₃N₄) composite material. The research focuses on evaluating the influence of copper doping on iron oxide rather than changing the ratio of Fe₂O₃/g - C₃N₄. Through systematic analysis of the structure and electrochemical characteristics of this composite material, researchers hope to find an electrode material with high specific capacitance, good cycle stability and energy density, thus promoting the development of supercapacitor technology.
### Research Background
Supercapacitors have become an important solution to meet the growing energy demand and environmental problems because of their advantages such as long life, high power density, cost - effectiveness, fast charge - discharge rate and safety. However, the application of traditional supercapacitors in flexible energy storage devices is limited by weight, volume and low capacitance. Therefore, researchers are committed to developing electrode materials with high specific capacitance and stability to improve the performance of supercapacitors. These materials mainly include carbon materials, conductive polymers and transition metal oxides.
### Research Methods
1. **Material Synthesis**:
- Graphitic carbon nitride (g - C₃N₄) was synthesized by the combustion method.
- Cu - Fe₂O₃/g - C₃N₄ nanocomposite materials with different copper doping ratios of 0%, 2%, 4%, 6% and 8% were prepared by the hydrothermal method.
2. **Material Characterization**:
- A variety of techniques such as X - ray diffraction (XRD), field - emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), X - ray photoelectron spectroscopy (XPS) were used to comprehensively characterize the composite materials.
3. **Electrochemical Performance Testing**:
- The electrochemical performance of the composite materials was evaluated by methods such as cyclic voltammetry (CV), galvanostatic charge - discharge (GCD) and electrochemical impedance spectroscopy (EIS).
### Main Findings
- **Structural Characterization**:
- XRD results show that the Cu - Fe₂O₃/g - C₃N₄ composite material was successfully synthesized, and copper doping has little influence on the crystal structure of Fe₂O₃.
- FESEM and TEM images show that copper doping leads to the formation of highly crystalline irregular nanostructures.
- XPS analysis confirms the elemental composition of the composite material, including Cu, Fe, O, N and C.
- **Electrochemical Performance**:
- The Fe₂O₃/g - C₃N₄ composite material with 6% Cu doping exhibits the highest specific capacitance, approximately 244.0 F g⁻¹ (at a scan rate of 5 mV s⁻¹).
- This composite material still maintains 94.22% of its capacity after 2000 charge - discharge cycles, showing excellent cycle stability.
- The maximum energy density reaches 5.31 W h kg⁻¹ (at a scan rate of 5 mV s⁻¹).
### Conclusion
This research successfully prepared a high - performance Cu - Fe₂O₃/g - C₃N₄ composite material, which significantly improved the electrochemical performance of supercapacitors. The Fe₂O₃/g - C₃N₄ composite material with 6% Cu doping is outstanding in terms of specific capacitance, cycle stability and energy density, and has broad application prospects.