Graphitization with Suppressed Carbon Loss for High-Quality Reduced Graphene Oxide
Jong-Chul Yoon,Xinyue Dai,Kyeong-Nam Kang,Jongha Hwang,Myung-Jun Kwak,Feng Ding,Ji-Hyun Jang
DOI: https://doi.org/10.1021/acsnano.1c02178
IF: 17.1
2021-07-01
ACS Nano
Abstract:An efficient reduction method to obtain high-quality graphene sheets from mass-producible graphene oxide is highly desirable for practical applications. Here, we report an <i>in situ</i> deoxidation and graphitization mechanism for graphene oxide that allows for high-quality reduced graphene oxide sheets under the low temperature condition (<300 °C) by utilizing a well-known Fischer–Tropsch reaction catalyst (CuFeO<sub>2</sub>). By applying modified FTR conditions, where graphene oxide was reduced on the catalyst surface under the hydrogen-poor condition, deoxidation with much suppressed carbon loss was possible, resulting in high-quality graphene sheets. Our experimental data and density functional theory calculations proved that reduction which occurred on the CuFeO<sub>2</sub> surface preferentially removed adsorbed oxygen atoms in graphene oxide sheets, leaving dissociated carbon structures to be restored to a near-perfect few-layer graphene sheet. TGA-mass data revealed that GO with catalysts released 92.8% less carbon-containing gases than GO without catalysts during the reduction process, which suggests that this process suppressed carbon loss in graphene oxide sheets, leading to near-perfect graphene. The amount of oxygen related to the epoxide group in the basal plane of GO significantly decreased to near zero (from 43.84 to 0.48 at. %) in catalyst-assisted reduced graphene oxide (CA-rGO). The average domain size and the density of defects of CA-rGO were 4 times larger and 0.1 times lower than those for thermally reduced graphene oxide (TrGO), respectively. As a result, CA-rGO had a 246 and 8 times lower electrical resistance than TrGO and CVD-graphene. With these performances, CA-rGO coated paper connected to a coin-cell battery successfully lit an LED bulb, and CA-rGO itself acted as an efficient catalyst for both the hydrogen evolution reaction and the oxygen evolution reaction.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c02178?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c02178</a>.SEM, TEM, and AFM images of catalysts and GO; additional data of CA-rGO (Raman, optical image, XRD, and electrical data); <i>I</i><sub>D</sub>/<i>I</i><sub>G</sub> ratio, XPS, UV–vis spectra, FT-IR spectra of samples prepared with different conditions; GC-mass analysis, TOF-SIMS, and ICP data for the reduction mechanism (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c02178/suppl_file/nn1c02178_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology