Core-shell-structured Ni@NiS2 encapsulated by N-doped carbon nanohorns growing on MOF to enhance oxygen evolution reaction performance at high current densities

Yanli Nan,Zhaoyu Wang,Zihan Zhang,Yuanyuan He,Yun Zhou

DOI: https://doi.org/10.1016/j.ceramint.2023.06.118

IF: 5.532

2023-06-01

Ceramics International

Abstract:To meet the requirements for commercial application, more and more attention has been paid to the oxygen evolution reaction (OER) catalytic performance under high-current conditions. In this article, carbon nanohorns (CNHs) filled with Ni nanoparticles can be obtained through a one-step method, and then the core-shell structured Ni@NiS2 encapsulated by N-doped carbon nanohorns (Ni@NiS2@CNHs) were obtained through a vulcanization process. Ni@NiS2@CNHs only requires a small potential of 400 mV to drive a high current density of 100 mA cm−2. Unfortunately, due to the strong agglomeration effect of nanopowders, the stability of Ni@NiS2@CNHs is slightly lower than that of other excellent catalysts. In this case, Ni+ deposited on the Ni@NiS2@CNHs was used as metal source to grow Ni-MOF by solvothermal method, ultimately obtaining Ni@NiS2@CNHs@MOF. It is found that this unique structure improves the electrocatalytic performance and stability of the composites. Thanks to the synergistic effect of multiphase nanostructures, Ni@NiS2@CNHs@MOF exhibited improved electrocatalytic performance. The underlying reason is that core-shell structured Ni@NiS2@CNHs can be stability and uniformly embedded on the layered structure of MOF, thus the long-time stability can be enhanced. To drive current density of 50 mA cm−2, 100 mA cm−2 and 200 mA cm−2 for OER, Ni@NiS2@CNHs@MOF only require potentials of 260 mV, 290 mV, and 310 mV, respectively, which is superior to most reported non noble metal catalysts. Combined with its excellent long-term stability, Ni@NiS2@CNHs@MOF can meet the requirements of commercial catalysts.

materials science, ceramics