Electrospun Polylactide—Poly(ε-Caprolactone) Fibers: Structure Characterization and Segmental Dynamic Response

Svetlana G. Karpova,Anatoly A. Olkhov,Ivetta A. Varyan,Oksana I. Khan,Andrey A. Botin,Anna V. Naletova,Anatoly A. Popov,Alexey L. Iordanskii
DOI: https://doi.org/10.3390/polym16101307
IF: 5
2024-05-08
Polymers
Abstract:Electrospun ultrathin fibers based on binary compositions of polylactide (PLA) and poly(ε-caprolactone) (PCL) with the various content from the polymer ratio from 0/100 to 100/0 have been explored. Combining thermal (DSC) and spectropy (ESR) techniques, the effect of biopolymer content on the characteristics of the crystal structure of PLA and PCL and the rotative diffusion of the stable TEMPO radical in the intercrystallite areas of PLA/PCL compositions was shown. It was revealed that after PLA and PCL blending, significant changes in the degree of crystallinity of PLA, PCL segment mobility, sorption of the Tempo probe, as well as its activation energy of rotation in the intercrystalline areas of PLA/PCL fibers, were evaluated. The characteristic region of biopolymers' composition from 50/50 to 30/70% PLA/PCL blend ratio was found, where the inversion transition of PLA from dispersive medium to dispersive phase where an inversion transition is assumed when the continuous medium of the PLA transforms into a discrete phase. The performed studies made it possible, firstly, to carry out a detailed study of the effect of the system component ratio on the structural and dynamic characteristics of the PLA/PCL film material at the molecular level.
polymer science
What problem does this paper attempt to address?
The problems that this paper attempts to solve mainly focus on the following aspects: 1. **Improving material properties**: Electrospun ultrafine fibers are prepared by mixing polylactic acid (PLA) with polycaprolactone (PCL) to improve the mechanical properties and thermal stability of single - polymer materials. PLA has good biocompatibility and biodegradability, but has problems such as brittleness and insufficient mechanical properties; while PCL has good flexibility and ductility, but its low melting point limits its application under high - temperature conditions. By mixing these two polymers, the properties of the two can be balanced, and a new biodegradable material with better comprehensive properties can be developed. 2. **Exploring structural and dynamic characteristics**: The structural characteristics and segmental dynamic responses of PLA/PCL blended fibers are studied. Specifically, by combining differential scanning calorimetry (DSC) and electron paramagnetic resonance (ESR) techniques, the effects of different PLA/PCL ratios on the crystalline structure of blended fibers, segmental mobility, and the rotational diffusion behavior of stable TEMPO radicals in the amorphous region are explored. 3. **Understanding phase - state transitions**: The phase - state distributions of PLA and PCL at different mixing ratios and their effects on material properties are studied. In particular, in the range of PLA/PCL ratios from 50/50 to 30/70, the phase - inversion phenomenon of PLA changing from a dispersion medium to a dispersed phase is explored, which is helpful for in - depth understanding of the relationship between the microstructure and macroscopic properties of the blended materials. 4. **Optimizing the preparation process**: PLA/PCL blended fibers are prepared by electrospinning technology, and the morphological characteristics of fibers at different mixing ratios are studied. For example, it is found that when the ratio of PLA to PCL is 50/50, the fibers exhibit a uniform cylindrical shape with almost no thickening, which may be related to the interaction between the two polymers during the mixing process. In summary, this paper aims to reveal the structural and dynamic characteristics of PLA and PCL blended fibers at different ratios through systematic research, thereby providing theoretical basis and technical support for the development of high - performance biodegradable materials.