Laser cladding state recognition and crack defect diagnosis by acoustic emission signal and neural network

Kaiqiang Li,Tao Li,Min Ma,Dong Wang,Weiwei Deng,Huitian Lu

DOI: https://doi.org/10.1016/j.optlastec.2021.107161

2021-10-01

Abstract:<p>Laser cladding technology uses a high-power laser beam to melt the substrate and metal powder at high temperature to form a molten pool. Relying on the spontaneous cooling of the molten pool, a metal cladding coating is formed on the substrate to strengthen the surface properties of the substrate metal. However, the typical defects such as cracks are easy to occur during the cladding process, which greatly affects the performance and quality of the cladded layer. This paper proposes a method for the state identification of cladding and the crack detection in the laser cladding process. By monitoring the acoustic emission signal during the laser cladding process, the current cladding state such as the status of laser power, scanning speed, and powder feed rate, and the occurrence of cracks are identified. By collecting the acoustic emission signal, the method first performs the data preprocessing for signal feature components according to the characteristic parameters of the signal maximum peak value and the energy of the emission signal samples, and then a deep learning neural network is applied to extract the feature vectors based on the two major characteristics of the signal. Finally, the current cladding states are recognized and the generation of cracks are detected based on the extracted feature vector and the identification through the neural network.</p>

optics,physics, applied

What problem does this paper attempt to address?

The paper attempts to address the problem of how to identify the current cladding state and detect common defects—cracks—during the laser cladding process. Laser cladding technology is a technique that uses a high-power laser beam to melt the substrate and metal powder at high temperatures to form a molten pool. Through the natural cooling of the molten pool, a layer of metal cladding is formed on the substrate to enhance the surface performance of the substrate metal. However, typical defects such as cracks are prone to occur during the cladding process, which can severely affect the performance and quality of the cladding layer. To tackle this challenge, the paper proposes a method based on acoustic emission signals and neural networks for state recognition and crack defect diagnosis during the laser cladding process. Specifically, this method monitors the acoustic emission signals during the laser cladding process to identify the current cladding state (such as the state of parameters like laser power, scanning speed, and powder feed rate) and the occurrence of cracks. By preprocessing the acoustic emission signals to extract signal feature components and applying deep learning neural networks to extract feature vectors, the method ultimately achieves the recognition of the current cladding state and the detection of cracks.

Laser cladding state recognition and crack defect diagnosis by acoustic emission signal and neural network

INTEGRATED TECHNOLOGY FOR DETECTION AND REPAIR OF MECHANICAL COMPONENT SURFACE FATIGUE MICROCRACKS USING PULSED LASER

Nondestructive detection of laser-cladding coating interface defects: a deep learning-enhanced laser ultrasonics approach

Detecting features of defect metal based on laser ultrasonic technique

Laser-induced thermal damage detection in metallic materials via acoustic emission and ensemble empirical mode decomposition

Reference-free Crack Detection and Localization by Nonlinear Laser Ultrasonic.

Detection and Quantification of Damage in Metallic Structures by Laser-Generated Ultrasonics

In-situ crack and keyhole pore detection in laser directed energy deposition through acoustic signal and deep learning

Dynamic evolution behavior of cracks for single-track and multi-track clads in laser cladding

A Technique Combining Laser Spot Thermography and Neural Network for Surface Crack Detection in Laser Engineered Net Shaping

Detection of solidification crack formation in laser beam welding videos of sheet metal using neural networks

Molten pool image processing and quality monitoring of laser cladding process based on coaxial vision

Classification of cracking sources of different engineering media via machine learning

Acquisition of heterogeneous constitutive relationship of Ni60 laser cladding layer based on nano-indentation experiment

Differential analysis of the influence mechanism of ultrasonic vibrations on laser cladding

An Overview of Laser Metal Deposition for Cladding: Defect Formation Mechanisms, Defect Suppression Methods and Performance Improvements of Laser-Cladded Layers

Crack Sensitivity Control of Nickel-Based Laser Coating Based on Genetic Algorithm and Neural Network

On the application of machine learning for defect detection in L-PBF additive manufacturing

Prediction of Geometric Characteristics of Laser Cladding Layer Based on Least Squares Support Vector Regression and Crested Porcupine Optimization

Laser ultrasonic inspection of surface and subsurface defects in materials based on deep learning

Quantitative analysis and experimental study of the influence of process parameters on the evolution of laser cladding