Abstract:Highlights•Micro/nano-scale porous Cu/CeO2 was prepared in one-step by a modified SCS method for the first time.•The introduce of metallic Cu improves the oxygen vacancy concentration of the CeO2.•The photocatalytic performance of 30% Cu/CeO2 is 4.3 times that of CeO2 with 120min.The Cu/CeO2 nanoporous composite material was prepared via a one-step and energy-saving method of solution combustion synthesis (SCS) for the first time. The phase composition, surface morphology and optical characteristics of Cu/CeO2 were studied. The results show that the SCS products are composed of cubic fluorite CeO2 and Cu. Due to the generation and escape of gas during the synthetic reaction, the SCS CeO2 shows porous structure, in which the mesopores (diameter 10–17 nm) nested in the wall of large pores (diameter 80–300 nm). X-ray photoelectron spectroscopy (XPS) outcomes indicate that the oxygen vacancy concentration of CeO2 increases (18.97%–30.93%) with the increase of Cu concentration. The decoration of Cu greatly enhances the catalytic activity of CeO2 nanomaterials. 30 wt% Cu/CeO2 composite material shows the best photocatalytic activities for the degradation of methyl orange (MO) (95.99%), which is about 4.3 times that of CeO2 at the same time (120min). UV-vis diffuse reflectance spectroscopy (DRS) results show that the semiconductor band gap is reduced with the addition of metallic Cu, which leads to the enhancement of photocatalytic activity. The free radical trapping experiments demonstrate that ·O2– and h+ were the main active species in the photocatalytic degradation of MO. Based on the above results, a hypothesized mechanism for enhanced photocatalysis of Cu/CeO2 nanomaterials was proposed: the porous structure provides more reactive sites and channels for mass transfer, and the presence of metallic Cu improves the oxygen vacancy concentration of CeO2 and then promote charge-carrier separation, which helps enhance the photocatalytic performance of Cu/CeO2.Graphical abstractMicro/nano-scale porous Cu/CeO2 was prepared in one-step by a modified SCS method for the first time. The porous structure provides more reactive sites and channels for mass transfer, and the presence of metallic Cu improves the oxygen vacancy concentration of CeO2 and then promotes charge-carrier separation, which improves the photocatalytic performance by 4.3 times.Download : Download high-res image (339KB)Download : Download full-size image

One-step solution combustion synthesis of micro/nano-scale porous Cu/CeO2 with enhanced photocatalytic properties

Nanoporous core–shell Cu@Cu2O nanocomposites with superior photocatalytic properties towards the degradation of methyl orange

Oxygen Vacancy Generation and Stabilization in CeO2–x by Cu Introduction with Improved CO2 Photocatalytic Reduction Activity

Facile synthesis of well-dispersed CeO2–CuOx composite hollow spheres with superior catalytic activity for CO oxidation

Boosting catalytic activity of Cu-Ce solid solution catalysts by flame spray pyrolysis with high Cu+ concentration and oxygen vacancies

Metal-organic framework derived hollow CuO/CeO2 nano-sphere: To expose more highly dispersed Cu-O-Ce interface for enhancing preferential CO oxidation

Synthesis, characterization and visible light-responsive photocatalysis properties of Ce doped CuO nanoparticles: A combined experimental and DFT+U study

Combustion Synthesis of Non-Precious CuO-CeO2 Nanocrystalline Catalysts with Enhanced Catalytic Activity for Methane Oxidation

Recent Advances of CeO2-Based Composite Materials for Photocatalytic Applications

Cu surface plasmon resonance promoted charge transfer in S-scheme system enhanced visible light photocatalytic hydrogen evolution

Nitrogen and sulfur co-doping CeO2 nanorods for efficient photocatalytic VOCs degradation

Construction of oxygen-rich vacancies and heterojunctions-coupled with different morphologies CeO2/mesoporous TiO2 framework structures and efficient photocatalytic CO2 reduction performance

Facile preparation of 3D ordered mesoporous CuOx-CeO2 with notably enhanced efficiency for the low temperature oxidation of heteroatom-containing volatile organic compounds

Co-embedding oxygen vacancy and copper particles into titanium-based oxides (TiO2, BaTiO3, and SrTiO3) nanoassembly for enhanced CO2 photoreduction through surface/interface synergy

Co2Cu1CeyOx Mixed Metal Oxide Nanoparticles with Oxygen Vacancies As Catalysts for Toluene Oxidation

Decoration of CeO 2 Nanoparticles on Cu/Co Bimetallic Oxide and Their Catalytic Performance

Enhanced photocatalytic activity of Ce-doped ZnO nanopowders synthesized by combustion method

Achieving simultaneous Cu particles anchoring in meso-porous TiO2 nanofabrication for enhancing photo-catalytic CO2 reduction through rapid charge separation

Constructing Efficient CuO-Based CO Oxidation Catalysts with Large Specific Surface Area Mesoporous CeO2 Nanosphere Support

Synthesis of novel CoOx decorated CeO2 hollow structures with an enhanced photocatalytic water oxidation performance under visible light irradiation

Hollow macroporous CeO2/β-Bi2O3 heterostructure sphere via one-step spray solution combustion synthesis for efficient photocatalysis