Low-temperature synthesis of a novel diboride ceramic with electromagnetic wave absorption properties
Chencheng Liu,Qingyun Chen,Xuhai Li,Zhonggang Xiong,Jiaxin Han,Guoyong Yang,Ke Yang,Yuezhong Wang,Yong Cheng,Nan Jiang
DOI: https://doi.org/10.1007/s10854-024-12044-2
2024-02-04
Journal of Materials Science Materials in Electronics
Abstract:At present, electromagnetic wave (EMW) absorption materials face challenges in terms of high efficiency, strong absorption, and low-cost preparation. Based on the thermodynamic behavior analysis of the initial raw materials and the design of temperature curves, a novel (Mo 0.2 Zr 0.2 Ti 0.2 Nb 0.2 Ta 0.2 )B 2 high-entropy ceramic with a small amount of oxide impurities was successfully synthesized under low-temperature conditions, using a simple thermal reaction method. Test analysis shows that the material has a two-dimensional nanostructured and excellent EMW absorption performance. Within the wide frequency range of 10.8–18.0 GHz, the reflection loss (RL) values of the samples are all less than − 10 dB. Especially, the minimum RL value (sample thickness 6 mm, at 11.4 GHz) can reach − 36.4 dB (99.9% wave absorption). Its excellent EMW absorption performance is related to its good impedance matching and multiple losses. This work provides a low-temperature preparation method for strong EMW absorption materials, and the performance and composition of the material system are adjustable.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied