Extremely Tough, Puncture-Resistant, Transparent, and Photoluminescent Polyurethane Elastomers for Crack Self-Diagnose and Healing Tracking
Xingxing Chen,Qianyun Zhong,Chenhui Cui,Li Ma,Shuang Liu,Qiang Zhang,Youshen Wu,Le An,Yilong Cheng,Shibo Ye,Xiaoming Chen,Zhen Dong,Quan Chen,Yanfeng Zhang
DOI: https://doi.org/10.1021/acsami.0c07727
2020-06-17
Abstract:Ensuring material performance reliability and lifetime is crucial for practical operations. Small cracks on the material surface are often detrimental to its safe operation. This study describes the development of a hydrogen bond-rich puncture-resistant polyurethane elastomer with supertoughness. The as-prepared polyurethane transparent films feature high tensile break strength (57.4 MPa) and great toughness (228 MJ m<sup>–3</sup>). Additionally, a facile, low-cost, crack self-diagnostic approach through photoluminescence using a small luminous pen is reported. The materials efficiently achieved self-healing at 90 °C after the crack formation. The change of fluorescence intensity on the crack can be used to track the self-healing process. Therefore, this work provides a guideline for the material design of supertough, puncture-resistant, transparent, and healable elastomers and a crack self-diagnosis and healing approach.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c07727?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c07727</a>.<sup>1</sup>H NMR of HPDU and HPPE samples; dependence of viscosity of DU aqueous solution on mass concentrations; FTIR, TGA, DSC, XRD, DMA, GPC, and 2D SAXS data of HPDU samples; swelling tests of HPDU4 sample in various polar solvents; transmittance of HPDU film after storage for 10 months at visible wavelengths; FTIR spectra of HPDU films fitted by Gauss Lorentz curves; stretchability test of HPDU, demonstrating a 31-fold deformation; strain–stress curves of HPPE films; cyclic strain–stress curves of HPDU films at different strains; recovery of residual strain on sample HPDU4 after relaxation for 60 min; cyclic strain–stress curves of HPDU films at 100% strain; monotonic stress–strain curves for uniaxial tension tests for HPDU4; strain–stress curves of HPDU10 after different healing times at 100 °C; fabrication procedure of stretchable conductor; schematic illustration of the stretchable conductor circuit; relative size of puncture tests; aggregation fluorescence enhancement properties of DU aqueous solutions at various concentrations under 365 nm excitation; aggregation-induced emission of DU in different mixed solvents; UV absorbance of various mass fractions of aqueous DU (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c07727/suppl_file/am0c07727_si_001.pdf">PDF</a>)Puncture test of material (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c07727/suppl_file/am0c07727_si_002.mp4">MP4</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology