Abstract:Metal-organic frameworks (MOFs) with different topologies formed by the self-assembly of sulfur-containing inorganic ligands, cobalt ions, and large ligands can be used to prepare electrocatalysts for water splitting in order to fully explore the advantages of MOFs in terms of structural tailoring and quantitative assembly. It is possible to avoid using an extradoped sulfur source to reduce waste as well as to disperse Co and sulfur elements evenly and controllably throughout the final material to maximize the overall synergistic effect. In this work, different kinds of bimetallic MOF materials containing sulfur can be synthesized very conveniently by using an economical and practical diffusion method. These materials are directly used as OER electrocatalysts, and the bimetallic MOFs have the best electrocatalytic performance when the ratio of Co to Fe is 6:4. The overpotential at a current density of 10 mA cm-2 was 260 mV, with a Tafel slope of 56 mV dec-1 and good stability. It was assembled with 20% commercial Pt/C material into a two-electrode system for all-water decomposition, and the decomposition voltage at 10 mA cm-2 was 1.81 V. From the electronic configuration microscopic point of view, the introduction of iron ions changed the original synergistic effect for Co-S-Co, which more easily led to the formation of high-valence Co3+ and finally produced highly active electrocatalytic sites. From a macroscopic point of view, the material produced in situ during the electrochemical reaction process not only retains the original 2D layered structure but also utilizes bubbles to produce a loose structure with defective sites. These structural features are advantageous because they provide not only an abundance of active sites and permeable channels but also the necessary interfaces and electron-transport channels for the formation of electrostatic charge-separation layers, making it easier to intercalate and delaminate the hydroxide ions. Furthermore, the changed hydroxyl ions and nitrogen and sulfur atoms on the channel surface may operate as interaction sites, increasing the surface characteristics, facilitating electron transfer, and reducing electron-transfer resistance. To summarize, the rational design of sulfur-containing layered MOF materials directly as water-splitting catalysts is a crucial next step in developing cost-effective, environmentally friendly, and low-energy-consumption electrocatalysts based on the findings of this study.

CoS2 particles loaded on MOF-derived hollow carbon spheres with enhanced overall water splitting

Mutually Beneficial Co3O4@MoS2 Heterostructures As a Highly Efficient Bifunctional Catalyst for Electrochemical Overall Water Splitting

Hierarchical flower-like CoS2-MoS2 heterostructure spheres as efficient bifunctional electrocatalyst for overall water splitting

ZIF-67 derived Mo-CoS2 nanoparticles embedded in hierarchically porous carbon hollow sphere for efficient overall water splitting

Formation of GO supported CoS2@MoS2 heterostructures with efficient electrocatalysis for water splitting

Microflower-like Co9S8@MoS2 heterostructure as an efficient bifunctional catalyst for overall water splitting

MOF-derived CoS2/WS2 electrocatalysts with sulfurized interface for high-efficiency hydrogen evolution reaction: Synthesis, characterization and DFT calculations

Co/CoS 2 heterojunction embedded in nitrogen-doped carbon framework as bifunctional electrocatalysts for hydrogen and oxygen evolution

Engineering the abundant heterointerfaces of integrated bimetallic sulfide-coupled 2D MOF-derived mesoporous CoS2 nanoarray hybrids for electrocatalytic water splitting

Abundant heterointerfaces in MOF-derived hollow CoS2–MoS2 nanosheet array electrocatalysts for overall water splitting

Pod-like 2D/3D-CoS2@CC Composite for Enhancing Electrocatalytic Hydrogen Evolution

A Janus cobalt nanoparticles and molybdenum carbide decorated N-doped carbon for high-performance overall water splitting

MOF-Derived CoS 2 @NiS-MoS 2 Ternary Composite Heterojunction Electrocatalyst for Efficient Water Splitting

Sulfur-doped cobalt molybdenum oxide with a hydrangea-like structure for bi-functionally efficient overall water splitting

MoS2@CoFe-MOF catalysts by one-pot hydrothermal synthesis enhanced electron interaction between MoS2 nanoflower and bimetallic MOF for efficient oxygen evolution

Co-metal–organic framework derived CoSe2@MoSe2 core–shell structure on carbon cloth as an efficient bifunctional catalyst for overall water splitting

Interfacial engineering of heterostructured carbon-supported molybdenum cobalt sulfides for efficient overall water splitting

Phase and composition controlled synthesis of cobalt sulfide hollow nanospheres for electrocatalytic water splitting

Highly Effective OER Electrocatalysts Generated from a Two-Dimensional Metal-Organic Framework Including a Sulfur-Containing Linker without Doping

Highly efficient electrocatalysts for overall water splitting: mesoporous CoS/MoS 2 with hetero-interfaces

Hierarchical 0D−2D Co/Mo Selenides As Superior Bifunctional Electrocatalysts for Overall Water Splitting