Abstract:Fe/N/C catalysts, synthesized through the pyrolysis of Fe-doped metal-organic framework (MOF) precursors, have attracted extensive attention owing to their promising oxygen reduction reaction (ORR) catalytic activity in fuel cells and/or metal-air batteries. However, post-treatments (acid washing, second pyrolysis, and so on) are unavoidable to improve ORR catalytic activity and stability. The method for introducing Fe3+ sources (anhydrous FeCl3) into the MOF structure, in particular, is a critical step that can avoid time-consuming post-treatments and result in more exposed Fe-Nx active sites. Herein, three different Fe doping strategies were systematically investigated to explore their influence on the types of active sites formed and ORR performance. Fe-NC(Zn2+), synthesized by one-step pyrolysis of Fe doped ZIF-8 (Zn2+) precursor which was obtained by adding the anhydrous FeCl3 source into the Zn(NO3)2•6H2O/methanol solution before mixing, possessed the highest Fe-Nx active sites due to the high-efficiency substitution of Zn2+ ions with Fe3+ ions during ZIF-8 growth, the strong interaction between Fe3+ ions and N atoms of 2-Methylimidazole (2-MIm), and ZIF-8's micropore confinement effect. As a result, Fe-NC(Zn2+) presented high ORR activity in the entire pH range (pH = 1, 7, and 13). At pH = 13, Fe-NC(Zn2+) exhibited a half-wave potential (E1/2) of 0.95 V (vs. reversible hydrogen electrode), which was 70 mV higher than that of commercial Pt/C. More importantly, Fe-NC(Zn2+) showed superior ORR stability in neutral media without performance loss after 5,000 cycles. A record-high open-circuit voltage (1.9 V) was obtained when Fe-NC(Zn2+) was used as a cathodic catalyst in assembled Mg-air batteries in neutral media. The assembled liquid and all-solid Mg-air batteries with high performance indicated that Fe-NC(Zn2+) has enormous potential for use in flexible and wearable Mg-air batteries.

Propagating Fe-N4 active sites with Vitamin C to efficiently drive oxygen electrocatalysis

Boosting the oxygen reduction performance of MOF-5-derived Fe-N-C electrocatalysts via a dual strategy of cation-exchange and guest-encapsulation

MnO synergizes with FeC–FeN in carbon nanofibers to boost oxygen reduction for zinc–air batteries

A Versatile Approach to Boost Oxygen Reduction of Fe‐N 4 Sites by Controllably Incorporating Sulfur Functionality

Nitrogen-carbon-encapsulated Fe3C nanoparticles as highly efficient earth-abundant oxygen reduction electrocatalysts

Simultaneously Integrate Iron Single Atom and Nanocluster Triggered Tandem Effect for Boosting Oxygen Electroreduction

Engineering Fe-N4 Electronic Structure with Adjacent Co-N2C2 and Co Nanoclusters on Carbon Nanotubes for Efficient Oxygen Electrocatalysis

A ferric citrate derived Fe-N-C electrocatalyst with stepwise pyrolysis for highly efficient oxygen reduction reaction

Nitrogen-carbon-encapsulated Fe 3 C Nanoparticles As Highly Efficient Earth-Abundant Oxygen Reduction Electrocatalysts

Engineering iron single atomic sites with adjacent ZrO2 nanoclusters via ligand–assisted strategy for effective oxygen reduction reaction and high–performance Zn–air batteries

Influence of different Fe doping strategies on modulating active sites and oxygen reduction reaction performance of Fe, N-doped carbonaceous catalysts

Enhancing activity and stability of Fe N C catalysts through co incorporation for oxygen reduction reaction

Shifting the Oxygen-Evolution Reaction Pathway via Cation Engineering to Activate Lattice Oxygen in Metal-Organic Frameworks

Fe-Co heteronuclear atom pairs as catalytic sites for efficient oxygen electroreduction

Sulfate Ions Induced Concave Porous S‐N Co‐Doped Carbon Confined FeC x Nanoclusters with Fe‐N 4 Sites for Efficient Oxygen Reduction in Alkaline and Acid Media

Synergistic Modulation of Multiple Active-Sites in Fe-N-C for High-Efficiency Oxygen Reduction Electrocatalysis

Coembedding Fe Single Atom-Coupled MoC Nanoparticles in N-Doped Hierarchically Porous Carbon Cubes for Oxygen Electroreduction

Regulating the coordination environment of atomically dispersed Fe-N 4 moieties in carbon enables efficient oxygen reduction for Zn-air batteries

Optimization of Fe and Co distribution on Fe-CoZn-ZIF derived polyhedral carbon via secondary adsorption for reversible catalysis of oxygen and zinc-air batteries

Mesoporous carbon promoting the efficiency and stability of single atomic electrocatalysts for oxygen reduction reaction

Highly active Fe centered FeM-N-doped carbon (M = Co/Ni/Mn): A general strategy for efficient oxygen conversion in Zn–air battery