Development of biodegradable plastic made from recycling of polypropylene (PP) with corn stalks powder

A. Anggono,Wijianto,A. Darmawan,C. Prasojo

DOI: https://doi.org/10.1088/1757-899X/673/1/012136

2019-12-10

IOP Conference Series: Materials Science and Engineering

Abstract:The objectives of the study are to develop biodegradable plastic composite and to investigate the mechanical characteristic and water absorption. It was made from polypropylene (PP) mixed with corn stalks powder. In this study, the weight fraction of polypropylene and powder was varied as 95% : 5%; 90% : 10%; 85% : 15%. For the water absorption test, the specimens were soaked in the water for 1, 7, and 14 days. The highest value of the tensile test was delivered from a specimen of 95% : 5% weight fraction. The tensile test of the soak specimen for 0, 1, 7, 14 days was obtained 17.41 MPa, 16.94 MPa, 16.11 MPa, 13.51 MPa respectively. The strain was 1.07, 1.19, 1.01, and 0.87%. The modulus of elasticity was 1686.74, 1500.42, 1712.1, and 1558.49 MPa. By adding the powder to the plastic, it was able to absorb water. The water absorption after 1, 7, and 14 days of water soak was 0.607, 1.468, and 4.651% respectively. The specimen of biodegradable plastic composites with a 95% : 5% ratio have compatible characteristics with commercial plastics and can be degraded easier than the origin plastic.

Environmental Science,Materials Science,Physics