Er-doped 0.96(K0.48Na0.52)(Nb0.965Sb0.035)O3-0.04(Bi0.5Na0.5)ZrO3 Multifunctional Ceramics with Good Temperature Stability

DOI: https://doi.org/10.1007/s11664-024-11163-0

IF: 2.1

2024-06-11

Journal of Electronic Materials

Abstract:Lead-free 0.96(K 0.48 Na 0.52 )(Nb 0.965 Sb 0.035− x Er x )O 3 -0.04(Bi 0.5 Na 0.5 )ZrO 3 (KNNS 0.035− x E x -BNZ) multifunctional ceramics were prepared by the conventional solid-state reaction method combined with the two-step sintering method. The results show that the ceramics doped with a moderate amount of Er 3+ show good piezoelectric properties and excellent temperature stability, while displaying bright up-conversion photoluminescence. Er 3+ -doping shifts the orthorhombic–tetragonal phase transition temperature ( T O-T ) down to below room temperature and enhances the temperature stability of the ceramics. For a 0.2 mol%Er 3+ -doped sample, the room-temperature piezoelectric constant d 33 reached 343 pC/N. The sample shows good resistance to thermal depoling as noted that the d 33 value remaining at more than 95% of that at room temperature when the temperature was increased to 230 °C. Relying on the luminescence behavior of rare earth Er 3+ ions, Er 3+ -doped samples exhibit a strong photoluminescence with a bright green up-conversion emission under excitation at 980 nm. Two green emissions, at 525 nm and 550 nm, corresponded to the transitions from 2 H 11/2 → 4 I 15/2 to 4 S 3/2 → 4 I 15/2 , and a weak red emission at 660 nm was assigned to the 4 F 9/2 → 4 I 15/2 transition obtained under the excitation of a 980-nm laser. The multifunctional properties in the Er-doped samples make them promising for multifunctional device applications.

engineering, electrical & electronic,materials science, multidisciplinary,physics, applied