Biorenewable Vegetable Oil Based Nonisocyanate Polyurethanes and Nanocomposites; Formulation, Characterisation, Biodegradation, Anticorrosion and Antifouling Coatings

Yasmin R. Sulthana,Dinesh Kumar Chelike,Sethilandavan A. Gurusamy Thangavelu

DOI: https://doi.org/10.1039/d3nj05862j

IF: 3.3

2024-02-18

New Journal of Chemistry

Abstract:To develop an efficient coating from biobased vegetable oil (castor oil, CO) towards the elimination of fossil resources as well as to prevent the impact of microorganisms on surface of maritime vessels, coatings of biorenewable and biodegradable nonisocyanate polyurethanes (NIPU) and nonisocyanate polyurethanes nanocomposites (NIPU-F) were formed. The biorenewable precursor, CO was modified as cyclic carbonate (CO-CC) substrate to form NIPU upon reaction with long chain aliphatic diamine (1,12-diaminododecane) via facile one pot reaction followed by film casting to recover NIPU films. Further, the protocol to form NIPU-F was executed by incorporation of synthesised amine-functionalised silica coated iron oxide nanoparticles (Fe3O4@SiO2-NH2) into NIPU matrix via covalent bond formation. Subsequently, the physicochemical (1H and 13C NMR, FT IR, XRD and VSM) thermal (TGA and DSC) and morphology (SEM, optical microscope and EDAX), characterization of NIPU and NIPU-F films were studied along with water contact angle, and biodegradation studies. The results highlighted that the synthesized NIPU shows the highest Tg value of 55oC with the average static water contact angle of 44o. The hydrophilic properties of above polymeric samples are identified as appropriate for applications in coatings towards antifouling, antibacterial and anticorrosion protection on submerged solid surfaces. As such the results from studies on NIPU and NIPU-F coatings inferred the remarkable resistance against E. coli bacteria with reduction of 99.7 and 88.7% respectively. Indeed, the settlements of algae like Spirulina platensis (S. platensis) on NIPU and NIPU-F diminished significantly by 71.2 and 52.9% respectively, as compared to that of the control sample. Furthermore, the electrochemical impedance spectroscopy (EIS) studies suggested that the exposure to 24h immersion period, the corrosion behaviour of both NIPU and NIPU-F attained a comparable level, with impedance magnitude |Z| ~1.6 *103 and ~1.7*103 ohm respectively. Herein, the demonstration of EIS studies in 3.5wt.% of NaCl and inhibition studies against microorganisms in marine environments by NIPU and NIPU-F pave new routes to apply such coating performance into a practical environment.

chemistry, multidisciplinary