Tunable magnetic structures in the helimagnet

Chun-Hao Lai,Chin-Wei Wang,Hung-Cheng Wu,Yu-Hui Liang,Andrew J. Studer,Wei-Tin Chen,Chao-Hung Du

DOI: https://doi.org/10.1103/physrevmaterials.8.054404

IF: 3.98

2024-05-08

Physical Review Materials

Abstract:We report the tunable magnetic structures in the helimagnet YBa(Cu1−xFex)2O5 by changing various Cu/Fe ratios. The magnetic properties and structures of the samples were studied by using neutron- and x-ray powder diffraction and susceptibility measurements. The parent material YBaCuFeO5 (YBCFO) exhibits two antiferromagnetic (AFM) transitions at TN1∼450 K and TN2∼175 K. At TN1 , YBCFO shows a commensurate (CM) spin ordering with a q- wave vector kc1=(1/21/21/2) , which transfers to a spiral magnetic ordering at TN2 with an incommensurate q -wave vector (1/2 1/2 1/2 ± δ ), δ being the incommensurability. Using neutron powder diffraction for samples with 0.490≤x≤0.505, TN2 was observed to systematically increase from 125 to 236 K as a function of the Cu/Fe ratio. For x=0.510 and 0.515, additional magnetic reflections with a propagation vector kc2=(1/21/20) appear below TN3∼245 and 269 K, respectively. This CM phase shows a collinear magnetic ordering. These transition temperatures are consistent with the AFM transitions of the magnetization data. Experiments were also conducted to synthesize the samples with different thermal treatments, demonstrating the TN2 and TN3 to be sensitive to the annealing conditions. These results can be understood within the framework of the random distributions of the dopants (impurities) at the B site of a double-perovskite lattice and demonstrate that the magnetic ordering in the helimagnet YBCFO can be systematically tuned by changing the Cu/Fe ratio. https://doi.org/10.1103/PhysRevMaterials.8.054404 ©2024 American Physical Society

materials science, multidisciplinary