Abstract:The treatment of dye pollutant and salts by nanofiltration membrane technology usually has the difficulty of low permeability and higher pressure in the case of maintaining a high rejection. In this study, high flux polyester membranes of β-cyclodextrin/trimesoyl chloride - multiwalled carbon nanotubes (β-CD/TMC-MWCNTs) were fabricated on a modified multiwalled carbon nanotubes (MWCNTs) substrate via interfacial polymerization (IP) process. The modified MWCNTs substrate was not only beneficial to modulating the permeation and distribution of aqueous phase monomer (β-cyclodextrin, β-CD), but also in favor of the formation of an ultrathin loose selective polyester active layer due to the porous network structure. The optimization experiments about the reaction time and monomer concentrations were conducted. The experimental results showed that the pure water flux of the as-prepared β-CD/TMC-MWCNTs membrane was 179.93 L m-2h-1 bar-1 (at the pressure of 0.1 MPa) when the reaction time of IP process was 5 min. The single dye removal efficiency of β-CD/TMC-MWCNTs membrane was 97.41% for Brilliant Green (BG) and 96.39% for Congo red (CR), respectively. The removal efficiency of dye/salt mixture by the membrane was above 84% for BG and over 98% for CR, respectively. The results indicated that the membrane had the efficient selective separation performance for the dye/salt mixture benefiting from the special molecular sieving architectures with the precisely intrinsic inner cavity of β-CD/TMC-MWCNTs membrane. Furthermore, the reusability, chlorine resistance, and antifouling ability of the β-CD/TMC-MWCNTs membrane was relatively excellent, and the membrane could effectively remove BG (>93%) and CR (>98%) simultaneously for mixed BG/CR dyes in real water body. These results suggested that the as-prepared β-CD/TMC-MWCNTs membrane had the potential of practical application in dye wastewater treatment.

Preparation of chlorine-resistant and regenerable antifouling nanofiltration membrane through interfacial polymerization using beta cyclodextrin monomers

Novel composite nanofiltration membranes containing zwitterions with high permeate flux and improved anti-fouling performance

Creating Smart Chlorine-Resistant Polyamide Reverse Osmosis Membranes Via Self-Healing Temperature-Responsive Nanocontainer Functionalization

Preparation and Characterization of Anti-Fouling Β-Cyclodextrin/polyester Thin Film Nanofiltration Composite Membrane

Preparation of self-healing and pH-responsive nanofiltration membranes with improved anti-fouling property for salt/dye separation

Improving the anti-fouling property and permeate flux of hollow fiber composite nanofiltration membrane using β-cyclodextrin

Antifouling and chlorine-resistant cyclodextrin loose nanofiltration membrane for high-efficiency fractionation of dyes and salts

Chlorine-resistant Polyester Thin Film Composite Nanofiltration Membranes Prepared with Β-Cyclodextrin

Fouling- and chlorine-resistant bilayer heterostructured Janus charged nanofiltration membranes constructed via novel electrospray polymerization-based method

Poly(vinyl alcohol)/polydopamine hybrid nanofiltration membrane fabricated through aqueous electrospraying with excellent antifouling and chlorine resistance

Preparation and Characterization of a Composite Nanofiltration Membrane from Cyclen and Trimesoyl Chloride Prepared by Interfacial Polymerization

Thin-film composite polyester nanofiltration membrane with high flux and efficient dye/salts separation fabricated from precise molecular sieving structure of β-cyclodextrin

Cyclodextrin-modified PVDF membranes with improved anti-fouling performance

Mechanistic Insights of a Thermoresponsive Interface for Fouling Control of Thin-Film Composite Nanofiltration Membranes.

Self-Cleaning Nanofiltration Membranes by Coordinated Regulation of Carbon Quantum Dots and Polydopamine

In Situ Chemical Modification with Zwitterionic Copolymers of Nanofiltration Membranes: Cure for the Trade-Off between Filtration and Antifouling Performance

Fabrication of anti-fouling polyester nanofiltration membrane for dye desalination

Fabrication of Thin-Film Composite Nanofiltration Membranes with Improved Performance Using Β-Cyclodextrin As Monomer for Efficient Separation of Dye/salt Mixtures

A Novel Composite Nanofiltration Membrane Prepared by Interfacial Polymerization of 2,2′-Bis(1-hydroxyl-1-trifluoromethyl-2,2,2-trifluoroethyl)-4,4′-methylenedianiline and Trimesoyl Chloride

Polyhydroxy Group Functionalized Zwitterion for a Polyamide Nanofiltration Membrane with High Water Permeation and Antifouling Performance

High Permselectivity Thin-Film Composite Nanofiltration Membranes with 3D Microstructure Fabricated by Incorporation of Beta Cyclodextrin