Properties and thermal neutron areal transmittance of a B 4 C filled thermoplastic elastomer based rubber composite
Boyu Wang,Tianyi Qiu,Jinnan Yin,Menghuai Wang,Shixin Ma,Qi Wang,Lin Yuan,Qinglong Fang,Guoqing Zhang,Yang Liu
DOI: https://doi.org/10.1016/j.nme.2022.101193
IF: 3.037
2022-05-06
Nuclear Materials and Energy
Abstract:In this paper, a kind of flexible shield for thermal neutron is fabricated through blending functional B 4 C powder with thermoplastic elastomer polystyrene- block -poly(ethylene- ran -butylene)- block -polystyrene(SEBS) in a banbury mixer, and weight fractions[(M B4C : M SEBS )%] of the composites are prepared as 10%, 20%, 30%, 40%, 60%, 100% respectively. B 4 C powders are well dispersed in the matrix of SEBS through microscopic observation, even without chemical interaction between the chemical groups of SEBS and the fillers. The elongations at break and tensile strengths of the B 4 C/SEBS composites deteriorate rapidly compared with the virgin sample, but it seems the tensile and tear strength could still maintain a satisfactory value suitable for preparing super flexible shields. The hardness of the composites is in the range of 15-25 HA. Based on a self developed nondestructive testing device, shielding abilities of the samples are estimated by neutron transmittance, 10 B areal density, linear attenuation coefficient, and thickness of half value layer. The neutron transmittance is 71.31%-32.43% corresponding to 10 B areal density ranging from 2.1873 mg/cm 2 to 17.6314 mg/cm 2 , linear attenuation coefficient is 0.1932-0.6435 mm -1 , and half value layer value is 3.59-1.08 mm. It is also proved that the neutron transmittance measured shows an exponential attenuation with the increase of 10 B areal density. The most importantly, the areal uniformity of neutron transmittance, with standard deviation less than 0.76%, is validated for the achievement of excellent attenuation of thermal neutrons in all directions. Consequently, results show excellent flexible and shielding performances of the functional composites.
nuclear science & technology