Synthesis of nest-like porous MnCo–P electrocatalyst by electrodeposition on nickel foam for hydrogen evolution reaction

Desheng Guo,Donghong Duan,Jie Gao,Xianxian Zhou,Shibin Liu,Yunfang Wang

DOI: https://doi.org/10.1016/j.ijhydene.2021.12.011

IF: 7.2

2022-02-01

International Journal of Hydrogen Energy

Abstract:It is very important to develop hydrogen evolution catalyst with high activity and low cost to solve energy crisis. The abundant non-precious metals and phosphides have attracted much attention and are expected to replace platinum catalysts. Herein, we report an approach to prepare nest-like porous MnCo–P electrocatalyst on the nickel foam by two-step electrodeposition. The prepared bimetallic phosphide MnCo–P3/NF has excellent hydrogen catalytic activity. In the 1 M NaOH solution, the current density of 10 mA cm−2 required overpotential is only 47 mV, its Tafel slope is 56.4 mV dec−1, and the higher current density 100 mA cm−2 required overpotential is only 112 mV. More importantly, the MnCo–P3/NF catalyst has a long-term stability of electrocatalytic hydrogen evolution. After 24 h catalytic hydrogen evolution test at a constant current density of 20 mA cm−2, its potential basically does not change. Furthermore, the current density only changes slightly after 1500 cycles of CV test. All these well prove that the prepared MnCo–P3/NF catalyst has a long-term hydrogen evolution stability. According to performance testing and morphological characterization, the MnCo–P3/NF has a high hydrogen catalytic activity and stability are due to its larger active area, lower interface charge transfer resistance and stronger mechanical stability. In , the study explores a method of preparing bimetallic phosphides as an efficient and stable hydrogen evolution catalyst.

energy & fuels,electrochemistry,chemistry, physical