Abstract:Si is one of the most promising anode materials for the next generation of lithium (Li) ion batteries (LIBs). Recently, we have developed a porous Si with a unique carbon coating structure (“carbon on Si” instead of “Si on carbon”). The nano-porosity of the materials absorbed most of volume expansion so the particles (between 3-5 mm) can retain their integrity during cycling instead of breakdown observed in bulk Si particles. Although single layer pouch cells (Si/NMC622, 62 mAh) with this porous Si anode and baseline electrolyte (1.2 M LiPF 6 in EC-EMC (3:7 by wt.) +10 wt.% FEC) can retain 91% capacity after 800 cycles, their calendar life is still far shorter from 10-year target required by electrical vehicles. In this work, we present a systematic investigation of the application of localized high concentration electrolyte (LHCE) to extend the cycle life and calendar life of Si-LIBs. A typical LHCE contains a Li salt (typically LiFSI) with high solubility in a common solvent (such as DMC), and a diluent (such as TTE) with minimal solubility of the Li salt. Compared with other electrolyte design, one distinct advantage of LHCE is that solvent and diluent in LHCE can be largely decoupled from each other: change in once components will have not significantly affect the functionality of other components. This characteristic of LHCE enables much more freedom in the electrolyte designs to satisfy different practical application needs (such as long cycle life, long calendar life, high rate, high temperature, and high voltage). For example, Si/NMC622 cells with a composition of LiFSI-2.15DMC-0.17VC-0.69FEC-4.31TTE (in molar ratio) have increased cycle life of Si/NMC622 pouch cells to 2000 cycles with 80% capacity retention at 25°C as compared with 1000 cycles when baseline electrolyte was used. However, this electrolyte is less stable when LiCoO 2 is used as the cathode, leading to rapid capacity loss at elevated temperatures (45°C). One possible reason for this is that cobalt in the cathode leads to more rapid decomposition of FEC than in the case of NMC622 at 45°C. On the other hand, the stability of LHCE is significantly affected by the amount of free (unbound) solvent (including DMC, VC, and FEC in the above example) in the electrolyte. By minimizing the amount of total free solvents, an electrolyte with a composition of LiFSI-2DMC-0.1EC-0.1FEC-3TTE has led to a long cycle life of Si/NMC622 cells at 25°C. Increasing the amount of main solvent in the electrolyte can further increase the conductivity of the electrolyte and significantly increase the charge/discharge rate of the cells. The long calendar life of Si-LIBs can be measured by accelerated tests at elevated temperatures (up to 55°C). Although FEC-containing electrolytes can increase the cycle life of Si-LIBs at room temperature, most Si-LIBs with FEC-containing electrolytes exhibit a rapid increase in impedance at elevated temperature, leading to a short projected-calendar-life. We designed a series of experiments to investigate the effect of FEC on the calendar life of Si-LIBs. The results clearly indicate that the formation of a high impedance interphase layer on the anode and cathode surfaces due to the decomposition of FEC at high temperatures is one of the fundamental reasons for the short calendar life of Si-LIBs. By replacing FEC with an alternative additive, a new LHCE electrolyte has been designed that led to much better cycling stability of Si-LIBs at 45°C (less than 5% capacity loss in 500 cycles) and much longer calendar life. More details of these investigations will be reported in this presentation.

Dual-Salt Localized High-Concentration Electrolyte for Long Cycle Life Silicon-Based Lithium-Ion Batteries

High‐Performance Silicon Anodes Enabled By Nonflammable Localized High‐Concentration Electrolytes

Solid Electrolyte Interface Film-Forming and Surface-Stabilizing Bifunctional 1,2-Bis((trimethylsilyl)oxy) Benzene As Novel Electrolyte Additive for Silicon-Based Lithium-Ion Batteries.

Extending Cycle Life and Safety of Si Based High Energy Li Ion Batteries Using Localized High Concentration Electrolytes

Bicomponent Electrolyte Additive Excelling Fluoroethylene Carbonate for High Performance Si-based Anodes and Lithiated Si-S Batteries

Design of Localized High Concentration Electrolytes for Fast-Charging Lithium-Ion Batteries

Rational Design of an In-Build Quasi-Solid-state Electrolyte for High-Performance Lithium-Ion Batteries with the Silicon-Based Anode

A Compatible Carbonate Electrolyte with Lithium Anode for High Performance Lithium Sulfur Battery

Nonflammable Localized High-Concentration Electrolytes with Long-Term Cycling Stability for High-Performance Li Metal Batteries

Dual Cross-Linked Fluorinated Binder Network for High-Performance Silicon and Silicon Oxide Based Anodes in Lithium-Ion Batteries

(Invited) Extending Cycle and Calendar Life of Si Based Li-Ion Batteries By Localized High Concentration Electrolytes

Multi-strategy Synergistic In-Situ Constructed Gel Electrolyte-Binder System for High-Performance Lithium-Ion Batteries with Si-based Anode

Localized High‐Concentration Electrolyte for All‐Carbon Rechargeable Dual‐Ion Batteries with Durable Interfacial Chemistry

Advanced Nonflammable Localized High‐Concentration Electrolyte For High Energy Density Lithium Battery

Localized High-Concentration Sulfone Electrolytes for High-Efficiency Lithium-Metal Batteries

Enhanced Salt Content and Stabilized Bilayer Passivation Interphase Toward Long-Life and High-Safety Anode-Free Lithium Battery

Localized High-Concentration Electrolyte (LHCE) for Fast Charging Lithium-Ion Batteries

Localized Medium Concentration Electrolyte with Fast Kinetics for Lithium Metal Batteries

Building stable solid electrolyte interphases (SEI) for microsized silicon anode and 5V-class cathode with salt engineered nonflammable phosphate-based lithium-ion battery electrolyte

(Invited) Improving Calendar Life of Si-Based Lithium-Ion Batteries By FEC/VC-Free Electrolytes

A Localized High-Concentration Electrolyte with Optimized Solvents and Lithium Difluoro(oxalate)borate Additive for Stable Lithium Metal Batteries