Temperature-Dependent Polymorphic Crystallization and Crystalline Structure of Unsaturated Polyesters Derived from cis -2-Butene-1,4-diol

Yang Yu,Ying Zheng,Junhao Liang,Xiaoli Sun,Yan Cao,Pengju Pan,Zhiyong Wei

DOI: https://doi.org/10.1021/acs.macromol.2c01698

IF: 5.5

2022-11-21

Macromolecules

Abstract:The poly­(cis-butene dicarboxylate)­s derived from cis-2-butene-1,4-diol and different diacids were synthesized, and their crystallization behavior and polymorphic structure were systematically investigated. The crystallization behavior of poly­(cis-butene dicarboxylate)­s depends on the number of methylene groups in polyester backbones. Poly­(cis-butene pimelate) (PcBP) and poly­(cis-butene azelate) (PcBAz) are semicrystalline, while poly­(cis-butene glutarate) (PcBG) is amorphous. Particularly, PcBP can form distinct crystal modifications with varying crystallization temperatures (T c). The α crystals are formed at T c above 23 °C, while the β crystals are formed at T c below 10 °C. The mixed crystals of α- and β-forms are generated at the intermediate temperature (10 ≤ T c < 23 °C). The melting points of α crystals were higher than those of β crystals, whereas the long period and crystalline thicknesses of α crystals were lower than those of β crystals. The crystal structures of polymrophic PcBP were determined: the α polymorph has a monoclinic unit cell with the parameters a = 0.725 nm, b = 0.895 nm, c = 1.698 nm, and β = 58.1°, and the β-form has a monoclinic unit cell with the parameters a = 0.839 nm, b = 0.965 nm, c = 1.670 nm, and β = 64.5°. The chain conformations in the α-form crystal are all-trans, whereas the conformation of β-form chains deviates from the all-trans and owns skew CH2–CH2–OC­(O) bonds (gauche bonds).

polymer science