Abstract:The evolution of phase composition and mechanical properties and the formation of oxide layers on Fe40–xNiCoCrAlx (x = 5 and 10 at.%) alloys in long-term oxidation at 900 and 1000°C were studied. In the initial cast state, depending on the aluminum content and valence electron concentration, the alloys contain only an fcc solid solution (VEC = 8 e/a) or a mixture of fcc and bcc phases (VEC = = 7.75 e/a). Thin continuous oxide scales containing Cr2O3 and NiCr2O4 spinel formed on the surface of both alloys oxidized at 900°C for 50 h. A further increase in the annealing time to 100 h leads to the formation of aluminum oxide Al2O3 in the scale on the Fe30Ni25Co15Cr20Al10 alloy, having high protective properties. An increase in the oxidation temperature to 1000°C results in partial failure of the protective layer on the alloy with 10 at.% Al. Long-term holding at 900°C (100 h) + 1000°C (50 h) does not change the phase composition of the Fe35Ni25Co15Cr20Al5 alloy matrix, being indicative of its high thermal stability. In the two-phase Fe30Ni25Co15Cr20Al10 alloy, the quantitative ratio of solid solutions sharply changes: the amount of the bcc phase increases from 4 to 54 wt.% and its B2-type ordering is observed. The mechanical characteristics of the starting alloys and those after long-term high-temperature annealing were determined by automated indentation. The hardness (HIT) and elastic modulus (E) of the cast Fe35Ni25Co15Cr20Al5 alloy are equal to 2 and 147 GPa, respectively, and decrease to 1.8 and 106 GPa after a series of long-term annealing operations. The Fe30Ni25Co15Cr20Al10 alloy shows the opposite dependence: HIT increases from 2.5 in the initial state to 3.1 GPa after annealing and E decreases from 152 to 134 GPa. This indicates that the Fe30Ni25Co15Cr20Al10 alloy is promising as a high-temperature oxidation-resistant and creep-resistant material.

Changing the Structure of a Single-Crystal Ni-Based Superalloy During Its High-Temperature Salt Corrosion at 750°C

A Study of the Hot Salt Corrosion Behavior of Three Nickel-Based Single-Crystal Superalloys at 900 °C

Studies on Corrosion Behavior of a Single-Crystal Superalloy and Its Sputtered Nanocrystalline Coatings with Solid NaCl Deposit in O2 + 38 Vol.% H2O Environment at 700 °C

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

High-temperature Corrosion of an Fe–Ni-based Alloy HR6W under Various Conditions at 750 °C and 810 °C: Effect of the Temperature, Water Vapor, Simulated Ash and SO2

High-temperature oxidation and hot corrosion of Ni-based single crystal superalloy in the incubation stage

Influence of microstructure on the oxidation behaviour of the Ni-based single crystal superalloy AM1 between 850 and 1050 °C in air

The microstructure evolution and its effect on the mechanical properties of a hot-corrosion resistant Ni-based superalloy during long-term thermal exposure

Influence of Cr Content on Hot Corrosion and a Special Tube Sealing Test of Single Crystal Nickel Base Superalloy

Temperature-Dependent Morphological Evolution during Corrosion of the Ni-20Cr Alloy in Molten Salt Revealed by Multiscale Imaging

Composition Design, Phase Transitions of a New Polycrystalline Ni-Cr-Co-W Base Superalloy and Its Isothermal Oxidation Dynamics Behaviors at 1300 °C

Oxidative Corrosion Mechanism of Ti2AlNb-Based Alloys during Alternate High Temperature-Salt Spray Exposure

High Temperature Oxidation Behavior of the Wrought Ni-based Superalloy GH4037 in the Solid and Semi-Solid State

Structural Evolution of a Ni Alloy Surface During High-Temperature Oxidation

Research on Hot Corrosion Behavior of DZ40M and K452 Superalloys in NaCl Molten Salt

Isothermal short‐term oxidation behavior of MAR‐M246 nickel‐based superalloy at 800°C and 1000°C

Stability of Microstructure and Mechanical Properties of A Ni-Based Superalloy for Advanced Ultra-Supercritical Fossil Power

ISOTHERMAL OXIDATION BEHAVIOR OF A SINGLE CRYSTAL NICKEL-BASED SUPERALLOY

Influence of alloying elements on hot corrosion resistance of nickel-based single crystal superalloys coated with Na2SO4 salt at 900 °C

An investigation on hot corrosion behavior of Al 0.4 MnCrCoFeNi high entropy alloy in different molten salts at 750 °C

Structural State of High-Entropy Fe40–xNiCoCrAlx Alloys in High-Temperature Oxidation