Abstract:Nano‐XCT analysis for batteries: This study compares scanning electron microscopy images and nano X‐ray computed tomography scans of pristine and cycle‐aged battery electrodes. Structural changes over the cycle life are determined, and a quantitative analysis of the active material's gray scale value distribution reveals severe degradation near the separator interface, with a reciprocal relationship to particle radius. LiNi0.8Co0.1Mn0.1O2 has emerged as a promising electrode material for automotive lithium‐ion batteries due to its high specific discharge capacity, cost‐effectiveness, and reduced cobalt content. However, despite all mentioned beneficial attributes, the widespread adoption of this material class is impeded by active material degradation during cycling operation, which is linked to performance loss. This study compares scanning electron microscopy images and nano X‐ray computed tomography scans with a 3D reconstruction of pristine and cycle‐aged battery electrodes to determine structural changes over cycle life. Although a very moderate current rate was chosen for the cycle test, which suggests a homogeneous load across the entire electrode, particle fracture varied across electrode thickness and particle size. A quantitative analysis of the active material's gray scale value distribution reveals severe degradation near the separator interface with a reciprocal relationship to particle radius. Remarkably, particle shape and size remain relatively unchanged despite cracking, eliminating the need to adjust these parameters in aging simulations. Moreover, it underscores the practical significance of particle cracking, as it can significantly impact the electrode's performance. Thus, analyzing changes in particle shape and size alone is insufficient, and a comprehensive exploration of the particle interior using nano‐XCT is necessary.

Nondestructive Analysis of Commercial Batteries

(Invited) Understanding the Coupled Electrochemical-Mechanical Behavior of Materials for Improving the Performance and Durability of Lithium-Ion Batteries

Non-destructive characterization techniques for battery performance and lifecycle assessment

Electrochemical Non-Destructive Analysis of Commercial 18650 Cells

Failure-detecting Techniques for Commercial Anodes of Lithium-Ion Batteries

Multiscale correlative imaging reveals sequential and heterogeneous degradations in fast-charging batteries

A Review of Existing and Emerging Methods for Lithium Detection and Characterization in Li-Ion and Li-Metal Batteries

A Multi-scale Framework for Advancing Battery Safety Through Early Calorimetric Analysis of Materials and Components

Non-destructive Degradation Pattern Decoupling for Ultra-early Battery Prototype Verification Using Physics-informed Machine Learning

Battery safety: Fault diagnosis from laboratory to real world

Dynamic investigation of battery materials via advanced visualization: from particle, electrode to cell level

Degradation Analysis of Commercial Lithium-Ion Batteries

Novel Non-Destructive Detection Methods of Lithium Plating in Commercial Lithium-Ion Batteries under Dynamic Discharging Conditions

An Efficient Approach for Quantifying the Mechanical Degradation of Ni‐Rich NMC‐based Cathodes for Lithium‐Ion Batteries using Nano‐XCT Analysis

Degradation Diagnostics of Lithium-Ion Batteries Cycled Under Varying Conditions

Fast Diagnosis of Failure Mechanisms and Lifetime Prediction of Li Metal Batteries

The Role of Structural Defects in Commercial Lithium-Ion Batteries

A facile physics-based model for non-destructive diagnosis of battery degradation

Ultralow-field nuclear magnetic resonance for direct nondestructive observation of electrolyte composition in batteries

Application of Nondestructive Testing Technology in Device‐Scale for Lithium‐Ion Batteries

A Comprehensive Review of in Situ Measurement Techniques for Evaluating the Electro-Chemo-Mechanical Behaviors of Battery Electrodes