Enhanced specific capacitance of Ni foam coated Ag2MoO4 symmetric supercapacitor synthesized by hydrothermal method

R. Shejini,K. Mohanraj,J. Henry,G. Sivakumar,R. Akash,V. Sivashankar,Mohanraj, K.

DOI: https://doi.org/10.1007/s10854-024-12420-y

2024-03-30

Journal of Materials Science Materials in Electronics

Abstract:For electrochemical performance, a number of reports are available on the asymmetric capacitor based on Ag 2 MoO 4 nanoparticles. In this present work, we investigate, for the first time, the electrochemical performance of the symmetric supercapacitor on Ag 2 MoO 4 nanoparticles prepared via the hydrothermal technique. In XRD, the 0.2 M Ag 2 MoO 4 nanoparticles obtained the cubic crystalline structure, and their crystallite size was found to be 46 nm. Here, when Ag is doped into molybdenum oxide nanoparticles, the diffraction peaks are shifted towards lower diffraction angles due to the ionic radius of Ag + (1.26 Å) being larger than Mo 6+ (0.65 Å). The FTIR spectrum of 0.2 M Ag 2 MoO 4 nanoparticles reveals the stretching and bending vibrations for Mo–O–Mo and Ag–O bonds at 819 and 635 cm −1 , respectively. In electrochemical studies, the 0.2 M Ag 2 MoO 4 nanoparticles exhibited a specific capacitance of 536 F g −1 at 1 A g −1 . Besides, the capacitance retention of 97.3% was obtained after 2000 cycles. In the EIS measurement, we observed a small semicircle, indicating a lower equivalent series resistance resulting from improved diffusion of the electrolyte and ions. In a symmetric supercapacitor, the 0.2 M Ag 2 MoO 4 nanoparticles reached a voltage of 1.2 V between two identical single electrodes, with energy and power densities measured at 26.8 and 363.5 W kg −1 , respectively. Based on the above results, Ag 2 MoO 4 nanoparticles are a good material for electrochemical applications and the development of effective energy storage devices.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied