Oxygen vacancies engineered self-supported B doped Co3O4 nanowires as an efficient multifunctional catalyst for electrochemical water splitting and hydrolysis of sodium borohydride

Hefeng Yuan,Shumin Wang,Zizai Ma,Manab Kundu,Bin Tang,Jinping Li,Xiaoguang Wang

DOI: https://doi.org/10.1016/j.cej.2020.126474

IF: 15.1

2021-01-01

Chemical Engineering Journal

Abstract:<p>Developing earth abundant electrocatalyst is imperative to large-scale hydrogen production for transforming current fossil fuel-based economy into future renewable energy economy. In this paper, we report the synthesis of self-supported V_OB-Co₃O₄/NF nanowire arrays directly grown on Ni foam, which can serve as a trifunctional catalyst for producing hydrogen and oxygen by electrolyzing water in alkaline media or producing hydrogen via hydrolyzing alkaline NaBH₄ solution. The engineered boron and oxygen defects in Co₃O₄ nanowires prove to effectively modulate their electronic structure leading to the increased electrical conductivity and create a large quantity of electroactive sites. The resulting self-supported V_OB-Co₃O₄/NF electrode delivers a current density of 50 mA cm⁻² at overpotentials of 184 mV for hydrogen evolution reaction (HER) and 315 mV for oxygen evolution reaction (OER) in 1.0 M KOH with excellent stability and durability. The V_OB-Co₃O₄/NF as both cathode and anode requires 1.67 V to achieve a current density of 10 mA cm⁻² for overall water splitting reaction. Besides, V_OB-Co₃O₄/NF presents much higher hydrogen generation rate (HGR) of 7055 mL min⁻¹ g_catalyst⁻¹ with activation energy (E_a) of ca. 29.7 kJ mol⁻¹. for hydrolytic dehydrogenation of alkaline NaBH₄ solution, outperforming most of the reported non-noble metal-based catalysts and even precious metal catalysts.</p>

engineering, chemical, environmental