Manufacturing Options for Activated Carbons with Selected Synthetic Polymers as Binders

Iwona Skoczko,Ewa Szatyłowicz,Adam Tabor,Remigiusz Gumiński
DOI: https://doi.org/10.3390/ma17081753
IF: 3.4
2024-04-11
Materials
Abstract:Formed activated carbon (AC) is a multipurpose product with developed adsorption properties that is widely used in various areas of life. To create AC, hard coal has to go through various processes: grinding, granulation, carbonization, physical and/or chemical activation. Presented research was conducted in the professional company manufacturing activated carbons. Studied AC reached the demanded shape of grains thanks to binders added to granulation process. Research on the AC formed using new polymeric binders (applied so far in other branches: pharmacy and construction materials) is presented in this manuscript. Tested binders were not used before to manufacture ACs in the professional technological line. Such polymers as: sodium carboxymethylhydrocellulose (CMHC), poly[1-(2-oxo-1-pyrrolidinyl)ethylene] (POPE) and enriched methyl-hydroxypropyl cellulose MHPC were studied in this work. Conducted research has proven efficiency of 8% CMHC which allowed for proper granulation and carbonization and reached the best parameters. Single- and double-stage activation was investigated for AC with this binder. For newly manufactured AC BET surface and pore volume increased accordingly from 774 m2/g and 0.58 cm3/g (1-stage) to 968 m2/g and 0.72 cm3/g (2-stage). Chemical elemental features of surface of the best AC showed beside elementary carbon also calcium, silicon and aluminum ions as well as groups with an acidic character, phosphates, sulphates and chlorides. The new AC had a higher Mechanical Strength reaching 99.9% and a lower Ash content and Volatile Matter than AC manufactured with previous binder—molasse. The new AC is intended to be directed for full production line and implementation to usage after positive certification. It may be useful in water treatment. It will also find application in the treatment of industrial and municipal wastewater.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The paper primarily explores various options for manufacturing molded activated carbon (AC) using specific synthetic polymers as binders. The research aims to find a new, efficient binder to replace the traditional, hard-to-obtain, and performance-unstable molasses for large-scale production of activated carbon. Researchers selected three polymers as potential new binders: Carboxymethyl Hydroxyethyl Cellulose (CMHC), Poly[1-(2-oxo-1-pyrrolidinyl)ethylene] (POPE), and Hydroxypropyl Methylcellulose (MHPC). These polymers had not been previously applied in professional activated carbon production lines. During the research, these new binders were evaluated through laboratory tests and actual production line tests. The results showed that 8% CMHC exhibited the best effect, enabling the successful granulation and carbonization of activated carbon with excellent physical properties. Compared to activated carbon produced using molasses as a binder, the new activated carbon had a higher specific surface area (BET surface increased from 774 m²/g to 968 m²/g), larger pore volume (increased from 0.58 cm³/g to 0.72 cm³/g), higher mechanical strength (reaching 99.9%), lower ash content, and lower volatile matter content. Additionally, the new activated carbon also showed surface characteristics containing calcium, silicon, and aluminum ions, as well as acidic groups such as phosphates, sulfates, and chlorides. This new activated carbon is expected to be put into actual production after certification and is anticipated to be widely used in the field of water treatment, including industrial and municipal wastewater treatment. In summary, this research aims to develop a new method for producing activated carbon by using efficient and stable polymer binders to replace traditional binders, thereby improving the quality and application range of activated carbon products.