Abstract:Aim: (1) To assess the release of stable silver nanoparticles (AgNPs) of small scale dimension added to heat polymerized polymethyl methacrylate (PMMA) in 6 months. (2) Assessing the influence of incorporating minimal concentrations of stable AgNPs with nanoscale dimensions into heat polymerized PMMA over a 6 month period on its antifungal efficacy (AF), flexural strength (FS), and impact strength (IS). Settings and design: Incorporating nanoparticles with a very small scale may have minimal impact on mechanical properties due to their diminutive size. However, the influence of these small scaled nanoparticles on antimicrobial efficacy and potential escalation in toxicity to host cells through leaching remains unexplored. AgNPs were prepared using an Ultrasonic Probe sonicator and the addition of ammonia to obtain stabilized AgNPs (< 0.01 nm) of small scale dimension. The characterization of these AgNPs involved ultraviolet visible spectroscopy, X ray diffraction, Zetasizer, and transmission electron microscopy with energy dispersive spectroscopy (TEM). Materials and methods: The prepared AgNPs were then added in various percentages by weight (0%-0.5%) to fabricate 252 modified PMMA samples of sizes 10 mm × 3 mm (AF, n = 108), 65 mm × 10 mm × 3 mm (FS, n = 72), and 65 mm × 10 mm × 2.5 mm (IS, n = 72) as per ADA specification no. 12. These samples underwent testing for leaching out of AgNPs and efficacy against Candida albicans for 6 months. The effect on FS and IS was evaluated using the three point bending test and Charpy's Impact Tester, respectively. Statistical analysis used: Intergroup comparison of CFU between various concentrations of AgNP was done using the Kruskal-Wallis ANOVA test succeeded by Mann-Whitney test for pair wise comparisons. Difference in CFU of various concentrations over 6 months was seen using one way ANOVA test. Intergroup comparison of FS and IS was performed using a one way ANOVA test, followed by a post hoc Tukey's test for pair wise comparisons. Results: Repeated tests showed no leaching out of AgNPs from the denture base resin into the storage medium. All concentrations of AgNPs incorporated in resin showed inhibition of Candida growth. Intergroup comparison of FS and IS revealed highly statistically significant differences (F = 15.076, P < 0.01 and F = 28.266, P < 0.01) between the groups showing a reduction in strength. Conclusion: The AgNPs of small scale dimension incorporated into the denture base resin imparted a strong antifungal effectiveness against C. albicans, which did not decline during the study period and did not cause any release of nanoparticles. 0.5% showed the best antifungal efficacy. This may prove to be a viable and highly effective treatment for the prevention of Candida associated denture stomatitis. However, the inclusion of these particles resulted in a decrease in both FS and IS, and this reduction was directly proportional to the percentage of added AgNPs, with 0.5% demonstrating the least IS and FS.

Mechanical and microbiological properties of orthodontic resin modified with nanostructured silver vanadate decorated with silver nanoparticles (βAgVO 3 )

Antibacterial and white spot lesions preventive effect of an orthodontic resin modified with silver-nanoparticles

Effect of silver vanadate on the antibiofilm, adhesion and biocompatibility properties of denture adhesive

Application of Silver Nanoparticles to Improve the Antibacterial Activity of Orthodontic Adhesives: An In Vitro Study

Antimicrobial properties, cytotoxicity, colour and mechanical behavior of light-cured resin composites containing modified Novaron

The Impact of Orthodontic Adhesive Containing Resveratrol, Silver, and Zinc Oxide Nanoparticles on Shear Bond Strength: An In Vitro Study

Antimicrobial efficacy and bonding properties of orthodontic bonding systems enhanced with silver nanoparticles: a systematic review with meta-analysis

The Antifungal Effects and Mechanical Properties of Silver Bromide/cationic Polymer Nano-Composite-modified Poly-methyl Methacrylate-Based Dental Resin

The effects of nano-silver loaded zirconium phosphate on antibacterial properties, mechanical properties and biosafety of room temperature curing PMMA materials

Evaluation of the antibacterial activity of a conventional orthodontic composite containing silver/hydroxyapatite nanoparticles

Microorganism Adhesion Inhibited by Silver Doped Yttria-stabilized Zirconia Ceramics

In vitro Assessment of the Antimicrobial Properties of Orthodontic Bonding Materials

Investigation of mechanical properties, remineralization, antibacterial effect, and cellular toxicity of composite orthodontic adhesive combined with silver-containing nanostructured bioactive glass

Improving the Antibacterial Properties of Dental Bonding Materials Loaded with Silver Compounds

Antibacterial, cytotoxic and mechanical properties of a orthodontic cement with phosphate nano-sized and phosphorylated chitosan: An in vitro study

Silver nanoparticles incorporated dental restorative resin and its antibiofilm effect

Assessing the physico-mechanical, anti-bacterial, and anti-demineralization properties of orthodontic resin composite containing different concentrations of photoactivated zinc oxide nanoparticles on Streptococcus mutans biofilm around ceramic and metal orthodontic brackets: An ex vivo study

Orthodontic adhesive loaded with different proportions of ZrO2 silver‐doped nanoparticles: An in vitro μTBS, SEM, EDX, FTIR, and antimicrobial analysis

Evaluation of the Preventive Effect of Composites Containing Silver and TiO2 Nanoparticles on Demineralization around Orthodontic Brackets

Evaluating the antifungal effectiveness, leaching characteristics, flexural strength, and impact strength of polymethyl methacrylate added with small-scale silver nanoparticles - An in vitro study

The influence of adding modified zirconium oxide-titanium dioxide nano-particles on mechanical properties of orthodontic adhesive: an in vitro study