Abstract:Once the characteristic size of materials reaches nanoscale, the mechanical properties may change drastically and classical mechanisms of materials failure may cease to hold. In this paper, we focus on joint atomistic-continuum studies of failure and deformation of nanoscale materials. In the first part of the paper, we discuss the size dependence of brittle fracture. We illustrate that if the characteristic dimension of a material is below a critical length scale that can be on the order of several nanometres, the classical Griffith theory of fracture no longer holds. An important consequence of this finding is that materials with nano-substructures may become flaw-tolerant, as the stress concentration at crack tips disappears and failure always occurs at the theoretical strength of materials, regardless of defects. Our atomistic simulations complement recent continuum analysis (Gao et al 2003 Proc. Natl Acad. Sci. USA 100 5597 - 600) and reveal a smooth transition between Griffith modes of failure via crack propagation to uniform bond rupture at theoretical strength below a nanometre critical length. Our results may have consequences for understanding failure of many small-scale materials. In the second part of this paper, we focus on the size dependence of adhesion systems. We demonstrate that optimal adhesion can be achieved by either length scale reduction, or by optimization of the shape of the surface of the adhesion element. We find that whereas change in shape can lead to optimal adhesion strength, those systems are not robust against small deviations from the optimal shape. In contrast, reducing the dimensions of the adhesion system results in robust adhesion devices that fail at their theoretical strength, regardless of the presence of flaws. An important consequence of this finding is that even under the presence of surface roughness, optimal adhesion is possible provided the size of contact elements is sufficiently small. Our atomistic results corroborate earlier theoretical modelling at the continuum scale (Gao and Yao 2004 Proc. Natl Acad. Sci. USA 101 7851 - 6). We discuss the relevance of our studies with respect to nature's design of bone nanostructures and nanoscale adhesion elements in geckos.

Intrinsic vulnerabilities to mechanical failure in nanoscale films

Atomistic perspective on in situ nanomechanics

Flaw-driven Failure in Nanostructures

Development of Multi-Scale Computation Framework to Investigate the Failure Behavior of the Materials

Strain Field Around Individual Dislocations Controls Failure

A Study on the Collapse of Self-Similar Hardening Behavior of Nanostructures

Recent Findings on the Mechanical Responses of Nanostructures to Extreme Loading Conditions

Dynamic Solidification in Nanoconfined Water Films

Finite Deformation Mechanics In Buckled Thin Films On Compliant Supports

Cracking and Adhesion at Small Scales: Atomistic and Continuum Studies of Flaw Tolerant Nanostructures

Fracture Mechanism of Metallic Film with Nano to Sub-Micron Thickness on Polycrystalline Substrate

Atomistic and Continuum Studies of Flaw Tolerant Nanostructuresin Biological Systems

Shear failure in supported two-dimensional nanosheet van der Waals thin films

Quantitative predictions of diverse wrinkling patterns in film/substrate systems

Mechanical Failure of a Small and Confined Solid

Size-Dependent Thermomechanical Responses of Nano-Sized Multilayers

Strengthening Materials by Engineering Coherent Internal Boundaries at the Nanoscale

Effects of surface/interface elasticity on the screw dislocation-induced stress field in an elastic film–substrate system

Surface Effects on the Jump-in Instability of Nanomechanical Structures

A Nanoindentation Study of the Deformation Mode for Nanostructured Ductile/brittle Multilayers: Cracking Versus Shear Banding

Strain shielding from mechanically-activated covalent bond formation in nanoindentation