Chemical heterogeneity enhances hydrogen resistance in high-strength steels

Binhan Sun,Wenjun Lu,Baptiste Gault,Ran Ding,Surendra Kumar Makineni,Di Wan,Chun-Hung Wu,Hao Chen,Dirk Ponge,Dierk Raabe

DOI: https://doi.org/10.1038/s41563-021-01050-y

IF: 41.2

2021-07-08

Nature Materials

Abstract:Abstract The antagonism between strength and resistance to hydrogen embrittlement in metallic materials is an intrinsic obstacle to the design of lightweight yet reliable structural components operated in hydrogen-containing environments. Economical and scalable microstructural solutions to this challenge must be found. Here, we introduce a counterintuitive strategy to exploit the typically undesired chemical heterogeneity within the material’s microstructure that enables local enhancement of crack resistance and local hydrogen trapping. We use this approach in a manganese-containing high-strength steel and produce a high dispersion of manganese-rich zones within the microstructure. These solute-rich buffer regions allow for local micro-tuning of the phase stability, arresting hydrogen-induced microcracks and thus interrupting the percolation of hydrogen-assisted damage. This results in a superior hydrogen embrittlement resistance (better by a factor of two) without sacrificing the material’s strength and ductility. The strategy of exploiting chemical heterogeneities, rather than avoiding them, broadens the horizon for microstructure engineering via advanced thermomechanical processing.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the phenomenon in high - strength alloys (with strength higher than about 650 MPa) that the presence of hydrogen (H) leads to a sudden loss of the material's load - bearing capacity, namely hydrogen embrittlement (H embrittlement). This phenomenon has led to catastrophic and unpredictable failures of large - scale engineering structures during service. Steel accounts for about 90% of the global metal alloy market, which means that even a small improvement in its performance will have an impact on the whole world. However, high - strength steel is particularly vulnerable to hydrogen embrittlement because less than 1 part per million by weight (ppmw) of hydrogen is sufficient to cause a significant decline in its mechanical properties. This extreme sensitivity to hydrogen embrittlement, combined with the inevitable hydrogen intrusion during steel production and/or service, has raised particular concerns about the use of these materials in the current target carbon - free hydrogen - propulsion industries and emission - reduction transportation solutions.

The paper proposes a strategy based on the utilization of solute heterogeneity in the microstructural components of steel. By designing local compositional changes to enhance local crack resistance, buffer zones are created to prevent the rapid propagation of hydrogen - induced micro - cracks into the interior or along the hydrogen - attacked phases or interfaces. This method not only improves the material's intrinsic resistance to hydrogen, but also maintains the material's strength and ductility, thereby overcoming the problems existing in traditional methods (such as adding protective coatings or designing microstructures to inherently improve toughness), such as increased cost, reduced strain - hardening ability and/or reduced ductility under hydrogen - free conditions. In addition, this method has broad application prospects when dealing with various high - performance steels containing metastable austenite, including various TRIP - assisted advanced high - strength steels, metastable stainless steels and maraging - TRIP steels, and may provide important insights for other advanced metal processing technologies such as powder metallurgy and additive manufacturing.